For sustainable development in the construction industry, blast furnace slag has been used as a substitute for cement in concrete. In contrast, steel-making slag, the second largest by-product in the steel industry, is mostly used as a filler material in embankment construction. This is because steel-making slag has relatively low hydraulicity and a problem with volumetric expansion. However, as the quenching process of slag has improved recently and the steel making process is specifically separated, the properties of steel-making slag has also improved. In this context, there is a need to find a method for recycling steel-making slag as a more highly valued material, such as its potential use as an admixture in concrete. Therefore, in order to confirm the possibility of using electric arc furnace (EAF) oxidizing slag as a binder, a comparative assessment of the mechanical properties of concrete containing electric arc furnace oxidizing slag, steel-making slag, and granulated blast furnace (GBF) slag was performed. The initial and final setting, shrinkage, compressive and split-cylinder tensile strength of the slag concretes were measured. It was found that replacing cement with EAF oxidizing slag delayed the hydration reaction at early ages, with no significant problems in setting time, shrinkage or strength development found.

Strain sensors can indicate the conditions of concrete structures, but these sensors are only capable of measuring local behaviors of materials. To solve this problem, researchers have introduced conductive materials that can monitor the overall behavior of concrete structures. Steelmaking slag, which contains large amounts of iron oxide (Fe₂O₃), is conductive, and researchers have considered the addition of this material to improve concrete monitoring. In this study, mechanical and electrical properties of concrete containing steelmaking slag as a binder were evaluated. As the incorporation of steelmaking slag increased, the setting times were delayed, but the compressive strengths were similar within the replacement ratio of 15%. It was found that the addition of steelmaking slag with Fe₂O₃, the main ingredient of magnetite (Fe₃O₄), improved the electrical resistivity, piezoresistivity, and sensitivity of the concrete. Drying of the concretes resulted in an increase in electrical resistance and fractional change in resistivity (FCR). Expansion of steelmaking slag, due to contacting of free CaO and moisture under repeated loads, resulted in cracks in the concrete and affected the gauge factor (GF). This study demonstrates the possibility that the addition of steelmaking slag as a binder may provide an economical and environmentally-friendly solution to concrete strain monitoring.

There is increased interest in applying electromagnetic (EM) shielding to prevent EM interference, which destroys electronic circuits. The EM shielding’s performance is closely related to the electrical conductivity and can be improved by incorporating conductive materials. The weight of a structure can be reduced by incorporating lightweight aggregates and replacing the steel rebars with CFRP rebars. In this study, the effects of lightweight coarse aggregate and CFRP rebars on the mechanical and electrical characteristics of concrete were investigated, considering the steel fibers’ incorporation. The lightweight coarse aggregates decreased the density and strength of concrete and increased the electrical conductivity of the concrete, owing to its metallic contents. The steel fibers further increased the electrical conductivity of the lightweight aggregate concrete. These components improved the EM shielding performance, and the steel fibers showed the best performance by increasing shielding effectiveness by at least 23 dB. The CFRP rebars behaved similarly to steel rebars because of their carbon fiber content. When no steel fiber was mixed, the shielding effectiveness increased by approximately 2.8 times with reduced spacing of CFRP rebars. This study demonstrates that lightweight aggregate concrete reinforced with steel fibers exhibits superior mechanical and electrical characteristics for concrete and construction industries.

The application of electric arc furnace oxidizing slag (EAS) in high strength concrete (HSC) as the cementitious material is investigated in this study. The microstructure and mechanical properties of HSC with four different replacement ratios of EAS were evaluated and HSC with two replacement ratios of ground granulated blast furnace slag (GBS) was used for performance comparison. The results show that the HSC with EAS replacement ratios smaller than 15% undergo similar hydration processes and result in a similar final product when compared with those of NC-NN. Increases in EAS replacement ratio cause a reduction in Ca(OH)₂ content; this, in turn, leads to an increase in porosity and a reduction in compressive strength. In terms of shrinkage behavior under free conditions, mixtures with increasing replacement ratios of cementitious materials saw increasing shrinkage, with the HSC containing EAS being similar to the other specimens. The mixtures containing EAS saw a quite gradual decrease in their freezing and thawing resistance properties as the number of freeze–thaw cycles they underwent increased. However, the efficacy of HSC with less than 15% of EAS is similar to GBS; hence, EAS could replace cement in concrete for certain applications, which would lead to more environmental benefits.

Following the fourth Industrial Revolution, electronic and data-based technology is becoming increasingly developed. However, current research on enhancing electromagnetic interference (EMI) shielding and the physical protection performance of structures incorporating these technologies is insufficient. Therefore, in this study aiming for the improvement of EMI shielding and structural performance of structures, twelve concrete walls were fabricated and tested to determine their shielding effectiveness and drop-weight impact resistance. Concrete walls strengthened by three thickness types of high-strength, high-ductility concrete (HSDC) have been considered. The test results showed that the shielding effectiveness with strengthening thickness increased by approximately 35.6–46.2%. Specimens strengthened by more than 40% and 10% of the strengthening area ratio of single- and double-layer, respectively, exhibited more than 20 dB of shielding effectiveness. Moreover, the relationship between the damaged area ratio and shielding effectiveness was evaluated by means of the drop-weight impact test. The structural performance and EMI shielding effectiveness improved as the HSDC thickness increased.