Among main ways to provide an environmentally friendly energy and platform chemicals are the lignocellulosic conversion processes. The proper execution of this way will depend on the correct selection of lignocellulosic materials. A compelling plant is Leucaena leucocephala because its great variety of uses, its high biomass production and its leguminous nature. In this study, acid hydrolysis (130-170°C and 0.5-2% H2SO4, to extract valuable hemicelluloses) as pretreatment and pyrolysis of the solid residue (to get a gaseous fuel) as treatment have been used in its valorization. A laboratory-scale reactor was used for the pyrolysis experiments (550ºC, N2) for both Leucaena leucocephala, as raw material, and the solid residues after hydrolysis process and raw material. The amounts of CO, CO2 and H2 found in the raw material are similar to those found in the solids obtained after the different studied hydrolysis conditions. Moreover, the thermal behavior of studied solids has been studied by thermogravimetric analysis under nitrogen atmosphere at different heating rates (5, 10, 15 and 20 ºC min-1). Activation energy for all samples has been obtained by the Flynn-Wall-Ozawa method. The optimum value, in which a high relationship between recoverable hemicelluloses fraction and H2 concentration is found, under medium hydrolysis temperature (150ºC) has been obtained and was independent of the amount of acid added to the hydrolysis process

Background: Burning fast-growing trees for energy production can be an effective alternative to coal combustion. Thus, lignocellulosic material, which can be used to obtain chemicals with a high added value, is highly abundant, easily renewed and usually inexpensive. In this work, hemicellulose extraction by acid hydrolysis of plant biomass from three different crops (Chamaecytisus proliferus, Leucaena diversifolia and Paulownia trihybrid) was modelled and the resulting solid residues were used for energy production. Results: The influence of the nature of the lignocellulosic raw material and the operating conditions used to extract the hemicellulose fraction on the heat capacity and activation energy of the subsequent combustion process was examined. The heat power and the activation energy of the combustion process were found to depend markedly on the hemicellulose content of the raw material. Thus, a low content in hemicelluloses resulted in a lower increased energy yield after acid hydrolysis stage. The process was also influenced by the operating conditions of the acid hydrolysis treatment, which increased the gross calorific value (GCV) of the solid residue by 0.6–9.7% relative to the starting material. In addition, the activation energy of combustion of the acid hydrolysis residues from Chamaecytisus proliferus (Tagasaste) and Paulownia trihybrid (Paulownia) was considerably lower than that for the starting materials, the difference increasing with increasing degree of conversion as well as with increasing temperature and acid concentration in the acid hydrolysis. The activation energy of combustion of the solid residues from acid hydrolysis of tagasaste and paulownia decreased markedly with increasing degree of conversion, and also with increasing temperature and acid concentration in the acid hydrolysis treatment. No similar trend was observed in Leucaena diversifolia (Leucaena) owing to its low content in hemicelluloses. Conclusions: Acid hydrolysis of tagasaste, leucaena and paulownia provided a valorizable liquor containing a large amount of hemicelluloses and a solid residue with an increased heat power amenable to efficient valorization by combustion. There are many potential applications of the hemicelluloses-rich and lignin-rich fraction, for example as multi-components of bio-based feedstocks for 3D printing, for energy and other value-added chemicals.

Xanthan gum solutions have gained increasing interest for their use as environmentally friendly chemicals in the oil industry. Xanthan is compatible with most concentrate brines used for controlling formation damage and fluid loss. Particularly, formate brines reinforce the ordered structure of the biopolymer in solution, gel strength, and the specific gravity of the resulting fluid. In this paper, we studied the effect of thermal aging on the rheological behavior of xanthan solutions as a function of the concentration in potassium formate. Ionic strength below a threshold concentration does not prevent the degradation of the structure of xanthan after being submitted to aging at 165 °C. Aged solutions show an important loss of strength in their mechanical properties, lower pH, and higher content in furfural and hydroxymethylfurfural. Highly concentrated formate brines are necessary to maintain the strength of the rheological properties after exposure to high-temperature environments.

The operating conditions for the autohydrolysis of eucalyptus wood were optimized with a view to maximizing hemicellulose extraction while preserving the integrity of glucan. The influence of the operating conditions used in the soda–anthraquinone pulping of the solid phase resulting from the autohydrolysis process was examined. Autohydrolysis of the raw material at a liquid/solid ratio of 8 kg water/kg material at 180°C for 30 min was found to provide a commercially useful liquid phase containing most of the starting hemicellulose. The autohydrolysis treatment allowed the subsequent production of soda–anthraquinone cellulose pulp and paper with properties as good as or even better than those obtained without the pretreatment.