Phthalocyanine (H₂Pc) and its open-shell copper complex (CuPc) deposited on amorphous gold films have been studied by combining the outcomes of several synchrotron based spectroscopic tools (X-ray photoelectron spectroscopy, UV photoelectron spectroscopy and near-edge X-ray absorption fine structure, NEXAFS, spectroscopy) with those of density functional theory (DFT) calculations. The assignment of experimental evidence has been guided by the results of DFT numerical experiments carried out on isolated molecules. With specific reference to CuPc NEXAFS data collected at the N K-edge, they have been assigned by using the open-shell time-dependent DFT (TDDFT) in the framework of the zeroth order regular approximation (ZORA) scalar relativistic approach. The agreement between theory and experiment has been found to be satisfactory, thus indicating that the open-shell TDDFT (F. Wang and T. Ziegler, Mol. Phys., 2004, 102, 2585) may be used with some confidence to look into the X-ray absorption spectroscopy results pertinent to transition metal complexes. As far as the metal–ligand interaction is concerned, the combined use of NEXAFS spectroscopy and DFT outcomes ultimately testified the significant ionic contribution characterizing the bonding between the metal centre and the nitrogen atoms of the phthalocyanine coordinative pocket.

We report the influence of the native amorphous SiO(2) shell on the cathodoluminescence emission of 3C-SiC/SiO(2) core/shell nanowires. A shell-induced enhancement of the SiC near-band-edge emission is observed and studied as a function of the silicon dioxide thickness. Since the diameter of the investigated SiC cores rules out any direct bandgap optical transitions due to confinement effects, this enhancement is ascribed to a carrier diffusion from the shell to the core, promoted by the alignment of the SiO(2) and SiC bands in a type I quantum well. An accurate correlation between the optical emission and structural and SiO(2)-SiC interface properties is also reported.

In this work, the authors unveil the depedance of the tensile strain and the size of MoS ₂ monolayer grown by liquid precursor chemical vapor deposition.