Second-generation glucose biosensors are presently the mainstream commercial solution for blood glucose measurement of diabetic patients. Screen-printed carbon electrodes (SPCEs) are the most-used substrate for glucose testing strips. This study adopted hydrophilic and positively charged α-poly-l-lysine (αPLL) as the entrapment matrix for the immobilization of negatively charged glucose oxidase (GOx) and ferricyanide (FIC) on SPCEs to construct a disposable second-generation glucose biosensor. The αPLL modification is shown to facilitate the redox kinetics of FIC and ferrocyanide on the SPCEs. The SPCEs coated with 0.5 mM GOx, 99.5 mM FIC, and 5 mM αPLL had better sensitivity for glucose detection due to the appreciable effect of protonated αPLL on the promotion of electron transfer between GOx and FIC. Moreover, the SPCEs coated with 0.5 mM GOx, 99.5 mM FIC, and 5 mM αPLL were packaged as blood glucose testing strips for the measurement of glucose-containing human serum samples. The glucose testing strips had good linearity from 2.8 mM to 27.5 mM and a detection limit of 2.3 mM. Moreover, the 5 mM αPLL-based glucose testing strips had good long-term stability to maintain GOx activity in aging tests at 50 °C.

The sensing properties of immunosensors are determined not only by the amount of immobilized antibodies but also by the number of effective antigen-binding sites of the immobilized antibody. Protein A (PA) exhibits a high degree of affinity with the Fc part of IgG antibody to feasibly produce oriented antibody immobilization. This work proposes a simple method to control the PA surface density on gold nanostructure (AuNS)-deposited screen-printed carbon electrodes (SPCEs) by mixing concentration-varied PA and bovine serum albumin (BSA), and to explore the effect of PA density on the affinity attachment of anti-salbutamol (SAL) antibodies by electrochemical impedance spectroscopy. A concentration of 100 μg/mL PA and 100 μg/mL BSA can obtain a saturated coverage on the 3-mercaptoproponic acid (MPA)/AuNS/SPCEs and exhibit a 50% PA density to adsorb the amount of anti-SAL, more than other concentration-varied PA/BSA-modified electrodes. Compared with the randomly immobilized anti-SAL/MPA/AuNS/SPCEs and the anti-SAL/PA(100 μg/mL):BSA(0 μg/mL)/MPA/AuNS/SPCE, the anti-SAL/PA(100 μg/mL): BSA(100 μg/mL)/MPA/AuNS/SPCE-based immunosensors have better sensing properties for SAL detection, with an extremely low detection limit of 0.2 fg/mL and high reproducibility (<2.5% relative standard deviation). The mixture of PA(100 μg/mL):BSA(100 μg/mL) for the modification of AuNS/SPCEs has great promise for forming an optimal protein layer for the oriented adsorption of IgG antibodies to construct ultrasensitive SAL immunosensors.