Oxygen-containing functional groups tend to induce a strong interaction between solid adsorbents and iodine molecules, yet have not been systematically investigated. Herein, on the basis of a series of nitric acid-treated graphene oxide (GO) with different contents of oxygen functional groups for iodine adsorption, it was found that the iodine uptake capacity is proportionate to the oxygen content and the diversities of oxygen-containing groups. The density functional theory (DFT) calculation results also suggest that oxygen-containing groups result in strong interactions between iodine molecules and the adsorbents through a covalent bond-forming process, among which -OH groups possess a higher adsorption energy averagely. Such theoretical and experimental work deepens our understanding of the effects of oxygen functional groups on iodine adsorption and provides novel ideas for future design and synthesis of high-performance solid adsorbents for radioactive iodine.

Due to the unbalanced three-phase currents and the torque ripples and speed fluctuations to the drive caused by the current sampling errors of three-phase current sensors and corresponding signal processing circuits, the estimation on current sampling errors is of great importance to eliminate these adverse effects. The observer-based methods, however, present two defects: first, they could increase the computational burden to the drives, thus limiting their practical applications; second, their high dependence on the system speed or position feedback information might degrade the estimation accuracy. To solve these problems, this article proposed a fixed-point sampling method of lower branch flows and three phase-currents, which adopts the relations between the measured currents, rather than any complex algorithm, to estimate the current sampling errors. To coordinate with the proposed strategy, a fixed-point sampling scheme was accordingly rolled out. Compared with the observer-based methods, as a fixed-point one, much applicable to actual digital controllers, it could reduce the computational burden of the drive. Meanwhile, its effectiveness was verified by experimental results on a 1.5-kW IPMSM prototype, which showed accurate estimated current sampling errors and the effectively eliminated torque ripples and speed fluctuations.

Secondary electron emission (SEE) inhibition and vacuum instability are two important issues in accelerators that may induce multiple effects in accelerators, such as power loss and beam lifetime reduction. In order to mitigate SEE and maintain high vacuum simultaneously, open-cell copper metal foam (OCMF) substrates with Ti-Zr-V-Hf non-evaporable getter (NEG) coatings are first proposed, and the properties of surface morphology, surface chemistry and secondary electron yield (SEY) were analyzed for the first time. According to the experimental results tested at 25 °C, the maximum SEY (${\delta }_{max}$) of OCMF before and after Ti-Zr-V-Hf NEG film deposition were 1.25 and 1.22, respectively. The XPS spectra indicated chemical state changes of the metal elements (Ti, Zr, V and Hf) of the Ti-Zr-V-Hf NEG films after heating, suggesting that the NEG films can be activated after heating and used as getter pumps.

Laser ablation technique is a novel method for obtaining a surface with a low secondary electron yield (SEY) that can mitigate electron cloud in high-energy accelerators. Before the installation of laser processed aluminum alloy, surface cleaning is of the essence to reduce the contaminations of ultra-high vacuum systems for providing appropriate pressure for beam operation consequently. Laser processed aluminum alloy is one of the crucial candidates for the vacuum system construction of future accelerators. Moreover, ultrasonic cleaning is an essential procedure for most materials applied in vacuum systems. Therefore, in order to verify the stability of the laser created structures by ultrasonic cleaning and evaluate the impact of the cleaning on the SEYs, the surface topographies, and the surface chemistries of laser treated aluminum alloy, SEY measurements and related tests were performed. After ultrasonic cleaning, the SEYs of laser treated aluminum alloy increased from 0.99, 1.05, and 1.16 to 1.43, 1.74, and 1.38, respectively. Compared to the surface roughness of uncleaned laser treated aluminum samples, the cleaned laser treated ones decreased from 10.7, 7.5, and 14.5 to 9.4, 6.9, and 12.9, respectively. The results indicate that ultrasonic cleaning can induce the SEY increase of laser processed aluminum alloy. The correlative mechanism between the surface morphology, the surface chemistry, and SEY increase were analyzed for the first time.