Under certain operating conditions, rolling contacts have been shown to experience some challenges when lubricated with engine oils containing zinc dialkyldithophosphate (ZDDP) anti-wear additive. In order to better understand the main damage mechanisms during various operating conditions, further studies are needed. This article studies micro-pitting and wear damages of bearing steel surfaces under mixed lubrication conditions in a ball-on-disc setup, lubricated with different engine oils. Based on the results, micro-pitting and wear damage is shown to be highly case-dependent. In general, PAO-based engine oil tends to eliminate micro-pitting damage compared to mineral-based engine oil at less severe lubricating conditions. Moreover, a critical lambda was found for both oils, where the highest micro-pitting damage was observed.

Machine components are designed to endure increasingly severe operating conditions due to the strive for improved energy efficiency of mechanical systems. Consequently, lubricated non-conformal contacts must rely on thin lubricant films where the influence of surface topography on the lubricating conditions becomes significant. Due to the complexity of the multiphysical problem, approximate assumptions are often employed to facilitate numerical studies of elastohydrodynamically lubricated (EHL) contacts. In this work, the rough, time dependent, thermal EHL problem is solved with focus on two main analyses. The first analysis focuses on the influence of sinusoidal roughness and the difference between a thermal non-Newtonian approach and an isothermal Newtonian approach. The second analysis is focused on the lubricating mechanisms taking place when two-sided surface features overtake within the thermal EHL contact. The results indicate that the film thickness in the outlet of the contact may be significantly overestimated by an isothermal Newtonian approach and that differences in the high-pressure region may also occur due to viscosity variations in the inlet of the contact. Moreover, for the studied two-sided surface features, it became evident that not only the surface feature combination but also the overtaking position influence the film thickness and pressure variations significantly.

In order to adapt to increasingly stringent CO2 regulations, the automotive industry must develop and evaluate low cost, low emission solutions in the powertrain technology. This often implies increased power density and the use of low viscosity oils, leading to additional challenges related to the durability of various machine elements. Therefore, an increased understanding of lubricated contacts becomes important where oil viscosity–pressure and compressibility–pressure behavior have been shown to influence the film thickness and pressure distribution in elastohydrodynamic lubrication (EHL) contacts, further influencing the durability. In this work, a finite line EHL contact is analyzed with focus on the oil compressibility–pressure and viscosity–pressure response, comparing two oils with relatively different behavior and its influence on subsurface stress concentrations in the contacting bodies. Results indicate that increased pressure gradients and pressure spikes, and therefore increased localized stress concentrations, can be expected for stiffer, less compressible oils, which under transient loading conditions not only affect the outlet but also the edges of the roller.

A crankshaft roller bearing internal combustion engine (ICE) offers a five percent or more improvement in overall engine efficiency and, thereby, a reduction in a five percent of CO₂ emissions, compared to a plain bearing supported crankshaft. Current forged crankshaft steels represent the limiting factor of the rolling component, therefore, a replacement of the crankshaft steel is required. Apart from this, the tribology of the rolling contacts has been shown to be detrimental when lubricated with current engine oils. Therefore, this paper investigates the tribological performance of potential crankshaft bearing steels, i.e. DIN C56E2 (G55); DIN 50CrMo4 (G50); and DIN 100Cr6 (G3), while utilizing a state-of-the-art low viscosity 0W20 engine oil and under conditions prevalent to ICE. For this, damage mode investigation was performed in a disc-on-disc setup. Based on the results, wear damage of DIN 100Cr6 discs was shown to be dependent on the steel grade of which the counterpart disc was made from and surface hardness difference between both discs. In addition, surface fatigue and wear damage can be completely eliminated by selecting a proper surface roughness and hardness combination. Also, while under an elevated roughness level, engine oil was shown to promote both surface fatigue and wear damage through the work of ZDDP additives, which under extreme conditions can act as an extreme pressure (EP) additive. The residual stress measurements using the XRD technique revealed relatively high compressive residual stresses for G55 and G50 in comparison to G3 steel after surface induction hardening. In addition, no significant changes in residual stress for G55 and G50 were observed after the test. In contrast, relatively high tensile stress was observed for G3 near the surface region. This suggests that the most commonly used 100Cr6 bearing steel, in this case, is the most susceptible to surface fatigue.