We study the influence of surface passivating ligands on the optical and structural properties of zinc blende CdSe nanoplatelets. Ligand exchange of native oleic acid with aliphatic thiol or phosphonic acid on the surface of nanoplatelets results in a large shift of exciton transition energy for up to 240 meV. Ligand exchange also leads to structural changes (strain) in the nanoplatelet's core analysed by wide-angle X-ray diffraction. By correlating the experimental data with theoretical calculations we demonstrate that the exciton energy shift is mainly caused by the ligand-induced anisotropic transformation of the crystalline structure altering the well width of the CdSe core. Further the exciton reduced mass in these CdSe quantum wells is determined by a new method and this agrees well with the expected values substantiating that ligand-strain induced changes in the colloidal quantum well thickness are responsible for the observed spectral shifts. Our findings are important for theoretical modeling of other anisotropically strained systems and demonstrate an approach to tune the optical properties of 2D semiconductor nanocrystals over a broad region thus widening the range of possible applications of A^IIB^VI nanoplatelets in optics and optoelectronics.

In this paper we report for the first time on the room temperature template synthesis of germanium and silicon nanowires by potentiostatic electrochemical deposition from the air- and water stable ionic liquid 1-butyl-1-methylpyrrolidinium bis(trifluoromethylsulfonyl)amide ([Py_1,4]Tf₂N) containing GeCl₄ and SiCl₄ as a Ge and Si source, respectively. Commercially-available track-etched polycarbonate membranes (PC) with an average nominal pore diameter of 90–400 nm were used as templates. Ge and Si nanowires with an average diameter corresponding to the nanopores’ diameter and lengths of a few micrometres were reproducibly obtained. Structural characterization of the nanowires was performed by EDX, TEM, HR-SEM and Raman spectroscopy. Despite the rough surface of the nanowires, governed mostly by the original shape of the nanopore’s wall of the commercially-available PC membrane, preliminary structural characterizations demonstrate the promising prospective of this innovative elaboration process compared to constraining high vacuum and high temperature methods.