To effectively remove non-metallic inclusions from the steel during the flowing in a five-strand asymmetric tundish, the novel configuration of the impact pad was developed. For analysis, complex numerical modelling in the programme ANSYS Fluent was used. The Lagrangian Discrete Phase Model of inclusion tracking was applied. The distribution of inclusions, with sizes ranging from 2 µm to 100 µm and density from 2500 to 3500 kg·m⁻³, was considered only through the shroud tube. The residence time distribution (RTD) curves and inclusion removal efficiency were used for evaluation of steady state steel flow character depending on internal configuration of a tundish with an impact pad in two design modifications (Modification 1—M1, Modification 2—M2). The preliminary results showed that in the case of asymmetric geometry plays a role the computational mesh independency. The assembly method with cut cell approach was satisfactory even when the tundish geometry was changed. The RTD curves with an M1 showed a huge dead volume in the tundish. In the case with an M2, the RTD curves are more or less uniform for all casting strands, and the removal of inclusions to slag increased from about 55% up to 70% in comparison with M1.

This paper deals with the possibilities of using physical modelling to study the slag entrainment in the tundish. A level of steel in the tundish is changing during sequential continuous casting. The most significant decrease in the steel level occurs when replacing ladles. It is generally known that if the height of steel level in the tundish drops below a certain critical level, it may generate vortexes over the nozzles and as a consequence entrainment of tundish slag into individual casting strands can occur. Thus, it is necessary to identify the critical level of steel for specific operational conditions. In this paper, the development of physical modelling methodology is described as well as physical model corresponding to operational continuous casting machine No. 2 in Třinecké železárny, a.s. The obtained results are discussed.

The submitted article deals with the use of physical and numerical modelling to study the process of the steel flow in an asymmetric five-strand tundish that continuously casts steel. For the purposes of physical modelling, a 1:4-scale plexiglass model was used as the operating tundish, and for numerical modelling, the geometry of the operating tundish was created on a 1:1 scale. A model liquid (water) was used in the physical modelling of the melt flow process, while liquid steel was used as the standard flowing medium in the numerical modelling. We assessed the relevant operating parameters influencing the characteristics of the flow of the bath in the tundish—the shape of the turbulence inhibitor, the position of the ladle shroud in relation to the turbulence inhibitor and the distance between the ladle shroud orifice and the bottom of the turbulence inhibitor. The preliminary results show that optimal steel flow characteristic results are achieved by using the TI3-C configuration. The results from both modelling methods achieved the same characteristics, therefore verifying the results of each other and demonstrating that when taken together, the results of physical and numerical modelling can be considered sufficiently informative.

The aim of this paper will be to present new knowledge and experience from numerical and physical modelling of metallurgical processes at the Department of Metallurgy, VSB - Technical University of Ostrava in Czech Republic and to explain especially the principle of tundish process simulations. The numerical modelling was realized by the CFD program FLUENT. The paper describes the pre-processing, processing and post-processing phases of numerical modelling. The physical modelling of the steel flow verification is based on a monitoring of the time dependency of concentration changes during experiments for individual tundish outlets. There exist two basic methods of KCl concentration change utilization in this "water" physical tundish modelling methodology. The utilization of mentioned methods are discussed and possible future developments are outlined for research of tundish steel intermixing.Celem artykułu jest przedstawienie wyników i doświadczeń z numerycznego i fizycznego modelowania procesów metalurgicznych w Zakładzie Metalurgii, VSB - Uniwersytet Techniczny w Ostrawie (Republika Czeska) i wyjaśnienie zasady symulacji procesów mieszania stali w kadzi pośredniej. Program CFD FLUENT posłużył do modelowania numerycznego. W artykule opisano pre-processing, processing i post-processing modelowania numerycznego. Weryfikację modelowania fizycznego przepływu stali dokonano w oparciu o eksperymenty, w których monitorowano zmianę stężenia w czasie dla poszczególnych stref kadzi. Istnieją dwie podstawowe metody wykorzystania zmian stężenia KCl w wodzie. Omówiono wykorzystanie wymienionych metod i możliwości przyszłego rozwoju badań mieszania stali w kadzi pośredniej.Web of Science57129629