Semi-solid processing of aluminum alloys is a well-known manufacturing technique able to combine high production rates with parts quality, resulting in high performance and reasonable component costs. The advantages offered by semi-solid processing are due to the shear thinning behavior of the thixotropic slurries during the mold filling. This is related to the microstructure of these slurries consisting of solid, nondendritic, near-globular primary particles surrounded by a liquid matrix. This paper presents a review on the formation of this nondendritic microstructure, reports on the different proposed mechanisms that might be responsible, and illustrates the relationship between microstructure and properties, in particular, tensility, fatigue, wear, and corrosion resistance.

Semi-solid processing of alloys is nearing the end of its fifth decade in existence. This promising manufacturing route has undergone a number of changes over the past five decades and apart from certain successful industrial applications, it appeared that it had become a niche technology with limited applications, notably in the automotive and consumer product markets. Nevertheless, despite the strong competition of traditional casting and in particular die-casting processes, and the emergence of Additive Manufacturing (AM), there seems to be a resurgence in demand for Net-Shape Die Casting of Semi-solid alloys as testified by the high numbers of delegates at the 15th SSM Conference at Shenzhen, China in September 2018. What follows is a brief review of the historical development of the process as well as more recent developments with an eye to future prospects.

Two rolled plates of 7075 aluminum alloy were used as starting material. The plates were welded using a simultaneous double-sided friction stir welding (FSW) process. One way of obtaining feedstock materials for Semi-solid processing or thixoforming is via deformation routes followed by partial melting in the semi-solid state. As both the base plate materials and the friction weld area have undergone extensive deformation specimens were subjected to a post welding heat-treatment in the semi-solid range at a temperature of 628 °C, for 3 min in order to observe the induced microstructural changes. A comparison between the microstructural evolution and mechanical properties of friction stir welded plates was performed before and after the heat-treatment in the Base Metal (BM), the Heat Affected Zone (HAZ), the Thermomechanically Affected Zone (TMAZ) and the Nugget Zone (NZ) using optical microscopy, Scanning Electron microscopy (SEM) and Vickers hardness tests. The results revealed that an extremely fine-grained structure, obtained in the NZ after FSW, resulted in a rise of hardness from the BM to the NZ. Furthermore, post welding heat-treatment in the semi-solid state gave rise to a consistent morphology throughout the material which was similar to microstructures obtained by the thixoforming process. Moreover, a drop of hardness was observed after heat treatment in all regions as compared to that in the welded microstructure.

Two plates of thixoformed 7075 aluminum alloy were joined using Electron Beam Welding (EBW). A post-welding-heat treatment (PWHT) was performed within the semi-solid temperature range of this alloy at three temperatures, 610, 617 and 628 °C, for 3 min. The microstructural evolution and mechanical properties of EB welded plates, as well as the heat-treated specimens, were investigated in the Base Metal (BM), Heat Affected Zone (HAZ), and Fusion Zone (FZ), using optical microscopy, Scanning Electron Microscopy (SEM), EDX (Energy Dispersive X-ray Analysis), and Vickers hardness test. Results indicated that after EBW, the grain size substantially decreased from 67 µm in both BM and HAZ to 7 µm in the FZ, and a hardness increment was observed in the FZ as compared to the BM and HAZ. Furthermore, the PWHT led to grain coarsening throughout the material, along with a further increase in hardness in the FZ.