The Q235 steel plate butt joint was successfully welded by the laser K-TIG hybrid welding method. The effects of hybrid welding process parameters such as welding current, the distance between heat sources, laser power, laser defocusing amount, and welding speed on the coupled arc profile and welding process stability were studied. The results indicated that the laser deflects the K-TIG arc, and the deflection angle becomes smaller as the arc current increases. After K-TIG generates small holes, if the laser beam acts on the bottom of the keyhole, the welded depth can be further increased; however, the laser power has little effect on the welded depth. The distance between heat sources is the main factor affecting the state of laser-arc coupling. Optical microstructures of welded joints showed that the grains in the arc zone were coarser than those in the laser zone, and there are more columnar crystals in the fusion zone. The microhardness of the weld center is significantly higher than that of the base metal, up to 220 HV. At the same time, the change of tensile strength of the weld under the influence of a single parameter was analyzed, and it was found that tensile properties of the weld first increased and then decreased with the increase of K-TIG arc current I, heat source distance D, and welding speed V, respectively. With the increase of laser power P, it first decreased and then increased, and with the increase of laser defocusing amount $\mathsf{\delta }$f, it showed a downward trend.

A novel plasma-pulsed GMAW hybrid welding (plasma-GMAW-P) process is proposed for joining 6061 aluminum and zinc-coated steel. The results show that the change in welding heat input has little effect on the microstructure of the joint and the composition of the intermetallic compounds (IMCs) but only changes the thickness of the reaction layer (increased from 5 μm to 12 μm). when the plasma arc current is 20 A and the MIG current is 80 A, the welded joint obtained has the highest tensile-shear force. With the optimal process parameters, the weld strength obtained by filling ER4043 welding wire is the highest, accounting for 65% of the tensile-shear force of the base material. The effect of the plasma arc acting on the joint properties is studied through the microstructure and a tensile-shearing test. The action position of the plasma arc plays a significant role in the Al/steel interface, which directly influences the strength of the welded joints. Regardless of the plasma-GMAW-P style used to obtain the joints, Fe-Al IMCs appear at the interface. When the plasma arc is in front of the welding direction and the GMAW-P arc is in the rear, the tensile-shear force reaches the maximum of 3322 N.