A diversity of chemicals is used to produce fire retardants (FRs); some of the main group of chemicals are hazardous to the environment as well as to human life; however, expandable graphite (EG) can be a gateway to a more environmentally friendly FRs or intumescent fire retardants (IFRs). Researchers define intumescent as the swelling of a particular substance placed between a heat source and an underlying substrate when they are heated. EG is a material with extraordinary thermophysical and mechanical properties. The referred EG properties are unparalleled. EG is a low-density carbon material having a series of unique properties: developed specific surface, binder-free pressing capacity, stability to aggressive media, and low thermal conductivity. Therefore, EG is a promising material both for research work and for industrial applications. The primary goal of this literature review was to report current knowledge on the use of EG as a fire retardant for cellulose and cellulose-modified materials. EG is produced, among other methods, by thermal shock of graphite oxide under forming gas. When exposed to heat, EG will expand. The expansion mechanism was presented in this review. Equally important to this review is the knowledge related to cellulose thermal degradation and cellulose impact on the development of science and technology.

This article describes how crystalline or fibrous nanocellulose influences the mechanical properties of paper substrate. In this context, we used commercially available cellulose nanocrystals, mechanically prepared cellulose nanofibers dispersed in water or ethanol, and carboxy cellulose nanofibers. Selective reinforcement of the paper treated with the nanocellulose samples mentioned above was observed. The change in the fibre structure was assessed using scanning electron microscopy, roentgenography, and spectroscopy techniques. In addition, the effect of nanocellulose coating on physical properties was evaluated, specifically tensile index, elongation coefficient, Elmendorf tear resistance, Bendtsen surface roughness, Bendtsen air permeability, and bending strength. It can be concluded that the observed decrease in the strength properties of the paper after applying some NC compositions is due to the loss of potential disturbances in hydrogen bonds between the nanocellulose dispersed in ethanol and the paper substrate. On the other hand, significantly increased strength was observed in the case of paper reinforced with nanocellulose functionalized with carboxyl groups.

Due to the wider use of nanocellulose in various areas of economic life, better and more optimal methods of obtaining nanocellulose are constantly being sought. Therefore, an attempt was made to evaluate the hybrid cellulose treatment, based on the use of a chemical method combined with an ultrasound of medium frequency. The study employs two different starting materials (Södra Black R cellulose or microcrystalline cellulose), two types of chemical pre-treatments (acid hydrolysis or oxidation), and two sonication durations. It was found that the reduction fiber cross-sectional dimensions was the result of prolonged exposure of cellulose to the ultrasound. From Södra Black R and the microcrystalline cellulose nanometer scale, structures were obtained in the form of isolated fibers. The TEMPO reagent accelerated the degradation process of two cellulose varieties due to its oxidizing character. The resulting products had nanofibrous structures. Cellulose degradation as a result of the combined action of sonication and TEMPO activity progressed gradually. Places of fiber degradation were characterized by their longitudinal breakage and initiated the next stages of the defibering process.

Ineffectiveness of the chemicals applied so far for waterlogged wood conservation created the need to develop new more, efficient and reliable agents. As an alternative, a new method with the use of organosilicon compounds differing in chemical composition and molecular weight has been investigated. The results obtained show the potential of organosilicons as consolidants in waterlogged wood conservation able to effectively stabilise wood dimensions upon drying. The best wood stabilisers were low-molecular organosilicons enable to penetrate the cell wall as well as chemicals with functional groups capable of interacting with wood polymers and forming stabilising coatings on the cell wall surface. The best anti-shrink efficiency values were obtained for (3-Mercaptopropyl)trimethoxysilane, (3-Aminopropyl)triethoxysilane, 1,3-Bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane, reaching 98, 91 and 91%, respectively. Most of the applied organosilicons reduced wood hygroscopicity, which limits the risk of further dimensional changes of wood exposed to a variable air moisture content and potentially reduces wood biodegradation. In the light of our studies, the proposed method of waterlogged wood conservation with organosilicons is potentially reversible in the case of siloxanes and amino-silanes as well as retreatable, which complies with the requirements of the conservation ethics.