In this investigation, six groups of cemented coal gangue-fly ash backfill (CGFB) samples with varying amounts of kaolin (0, 10, 20, 30, 40, and 50%) instead of cement are prepared, and their mechanical properties are analyzed using uniaxial compression, acoustic emission, scanning electron microscopy, X-ray diffraction, and Fourier transform infrared spectroscopy. The uniaxial compressive strength, peak strain, and elastic modulus of CGFB samples decreased with the kaolin content. The average uniaxial compressive strength, elastic modulus, and peak strain of CGFB samples with 10% amount of kaolin are close to that of CGFB samples with no kaolin. The contribution of kaolin hydration to the strength of CGFB sample is lower than that of cement hydration, and the hydration products such as ettringite and calcium-silicate-hydrate gel decrease, thereby reducing strength, which mainly plays a role in filling pores. The contents of kaolin affect the failure characteristics of CGFB samples, which show tensile failure accompanied by local shear failure, and the failure degree increases with the kaolin content. The porosity of the fracture surface shows a decreasing trend as a whole. When the amount of kaolin instead of cement is 10%, the mechanical properties of CGFB samples are slightly different from those of CGFB samples without kaolin, and CGFB can meet the demand of filling strength. The research results provide a theoretical basis for the application of kaolin admixture in fill mining.

A comprehensive understanding of the mechanical properties of coal and rock sections is necessary for interpreting the deformation and failure modes of such underground sections and for evaluating the potential dynamic hazards. However, most studies have focused on horizontal coal–rock composites and the mechanical properties of inclined coal–rock composites have not been considered. To explore the influence of different confining pressures and inclined coal seam thicknesses on the mechanical properties and failure characteristics of rock–coal–rock (RCR) composites, a numerical model based on the particle flow code was used to perform simulations on five inclined RCR composites at different confining pressures. The results show that the mechanical properties and failure characteristics of the RCR composites are affected considerably by the inclined coal seam thickness and the confining pressure. (1) When the inclined coal seam thickness is constant, the elasticity modulus of the inclined RCR composite increases nonlinearly with the confining pressure at first, and then remains constant. At the same confining pressure, the elasticity modulus of the inclined RCR composite decreases nonlinearly with the inclined coal seam thickness. (2) When the confining pressure is constant, the peak stress of the inclined RCR composite decreases with the increase of the inclined coal seam thickness. When the inclined coal seam thickness is constant, the peak stress increases with the confining pressure. (3) As the inclined coal seam thickness increases, the peak strain of the inclined RCR composite first decreases rapidly, and then remains constant when there is no confining pressure. When the confining pressure is between 5 and 20 MPa, the peak strain of the inclined RCR composite gradually increases. (4) In the absence of confining pressure, there are few microcracks in the rock at an inclined coal seam thickness of 10 mm, whereas all the other cracks are in the coal section. When the confining pressure ranges between 5 and 20 MPa, the failure modes of the RCR composite can be divided into Y- and X-types.

The traditional method to design coal pillar for lateral roof roadway was established based on the mining‐induced strata movement contour which is considered as a straight line, while ignoring the variations of the internal strata deformation law as well as stress distribution characteristics. In order to make up for this deficiency, in this study, evolution of mining‐induced stress in the overlying strata was simulated using physical and numerical simulations, and a method to design coal pillar for lateral roof roadway based on mining‐induced stress was proposed. The results indicate that the stress of the overlying strata is redistributed during excavation, and the stress distribution can be divided into a stress‐relaxation area, a stress‐concentration area, and an in situ stress area. The contour line of 1.05 times the in situ stress is used to define the mining‐induced stress contour. Stress inside the contour is redistributed while outside the contour the overlying strata are still within the in situ stress area. Mining‐induced stress contour presents a concave‐upward type from coal seam to the overlying strata that cannot be merged into a straight one due to their different characteristics of movement and deformation. With this in mind, this study proposed a method to design the width of coal pillar for lateral roof roadway according to the mining‐induced stress contour. According to mining‐induced stress contour, the width of coal pillar for lateral roof roadway of longwall panel 31100 is 160 m, and the maximum deformation of the roadway is 270 mm. The new method can definitely meet engineering demands.

Natural rock masses often contain heterogeneous structures with varying sizes, non-uniform distributions, and strengths, which influence the mechanical response characteristics and crack propagation modes under loading. Furthermore, heterogeneous structures can affect the stability of the rock mass, in serious cases, leading to geotechnical and mining engineering disasters. In the present work, a parallel-bond model (PBM)-based numerical simulation using Particle Flow Code (PFC) was carried out to study the strength and failure characteristics of sandstone specimens with heterogeneous structures under different loading rates. The results show that the peak strength increases with the increasing loading rate. In addition, all of the initial cracks occurred at the edges of the heterogeneous structures of specimens under different loading rates. The greater the loading rate, the greater the stress concentration degree at the edge of the heterogeneous structures, the greater the dissipated energy as the sandstone specimens with heterogeneous structures suffer damage, the more intense the acoustic emission activity, and the greater the damage degree of the specimens. The number of cracks generated in sandstone specimens with heterogeneous structures increases gradually with the increasing loading rate during the initial loading stage, and gradually decreases after the specimens are damaged. Cracks propagate and develop from the upper right region to the lower right region of the specimens, forming crack groups that rapidly penetrate the specimens, leading to failure. Under different loading rates, the final failure behavior of the sandstone specimens with heterogeneous structures changes from an inverted V-type to θ-type, then gradually evolves to O-type failure.

In this investigation, the uniaxial short-term creep tests with multi-step loading were conducted on the sandstone-coal composite samples, and the characteristics of creep strength, creep deformation, acoustic emission (AE), and creep failure of composite samples were studied, respectively. The creep strength of the composite sample decreased with the stress-level duration, which was mainly determined by the coal and influenced by the interactions with the sandstone. The creep deformation and damage of sandstone weakened the deformation and damage accumulation within the coal, resulting in the larger strength for the composite sample compared with the pure coal sample. The axial creep strain of composite sample generally increased with the stress-level or the stress-level duration under same conditions. The AE characteristics of composite sample were related to the creep strain rate, the stress level, the stress level duration, and the local failure or fracture during creep loading. The micro or macro failure and fracture within the composite sample caused the rise in the axial creep strains and the frequency and intensity of AE signals, especially the macro failure and fracture. The creep failures of composite samples mainly occurred within the coal with the splitting ejection failure accompanied by the local shear failure, and no obvious failures were found within the sandstone. The coal in the composite sample became more broken with the stress-level duration.