A 365-nm UV LED was fabricated based on embedded nanoporous AlGaN distributed Bragg reflectors (DBR) by electrochemical etching. The porous DBR had a reflectance of 93.5% at the central wavelength of 365 nm; this is the highest value of porous AlGaN DBRs below 370 nm which has been reported so far. An innovative two-step etching method with a SiO₂ sidewall protection layer (SPL) was proposed to protect the n-AlGaN layer and active region of UV LED from being etched by the electrolyte. The DBR-LED with SPL showed 54.3% improvement of maximal external quantum efficiency (EQE) and 65.7% enhancement of optical power at 100 mA without any degeneration in electrical properties, compared with the un-etched standard LED sample. This work has paved the way for the application of electrically-pumped UV LEDs and VCSELs based on nanoporous AlGaN DBRs.

In this paper, size effects on optical performance of blue light-emitting diodes (LEDs) are investigated. The essential physical mechanism is studied by fabricating LEDs with various sizes of the active area and testing optical characteristics. It is found that micro-LEDs have better light extracting efficiency and thermal dissipation compared with broad-area LEDs, which is likely due to the small ratio of perimeter and active area. Furthermore, micro-LEDs are more beneficial for displays due to the stable wavelength under the low pulse width modulation (PWM) current density.

We present a novel stackable luminescent device integrating a blue light emitting diode (LED) with a red organic LED (OLED) in series. The anode of the OLED is connected with the cathode of the LED through a via in the insulation layer on the LED. The LED–OLED hybrid device is electroluminescent and two electroluminescence (EL) peaks (the blue peak around 454 nm and the red peak around 610 nm) are observed clearly. The effect of the indium tin oxide (ITO) layer on the device performance is analyzed. Compared with the individual LED and OLED, their combination shows great potential applications in the field of white lighting, plant lighting, and display.