Three kinds of drag reducer were synthesized by inverse emulsion polymerization and named PHWAM-1, PHWAM-2, and PHWAM-3. Drag reduction (DR) tests showed that the three drag reducers have different DR characteristics in fresh water and various saline waters because of their different types of hydrophobic monomers. PHWAM-1, without hydrophobic monomers, performs better in fresh water, while PHWAM-2 and PHWAM-3, with hydrophobic monomers, perform better in brine. In addition, PHWAM-3, which has twin-tailed hydrophobic monomers, performs best in high-concentration brine. Measurements of micro-particle size and observations of spatial structure suggest that although the stronger hydrophobic polymer has no DR advantage over a linear polymer in fresh water, the molecular chains form a mutually associative supporting structure that improves the DR performance over that of a linear polymer in high-concentration brine.

Because of their high viscoelasticity, Hydrophobic Associative Water-Soluble Polymers (HAWSPs) have been widely used in many industrial fields, especially in oilfield flooding and fracturing. However, one major problem which limits the wide applications of HAWSPs is their weak resistance to high temperatures. Once the temperature increases over 100 °C, the viscosity of the fracturing fluid decreases rapidly, because high temperatures reduce fluid viscosity by oxidizing the polyacrylamide chains and weakening the association of hydrophobic groups. To improve the high temperature resistance of one HAWSP, a triple-protection strategy was developed. First, rigid N-vinyl-2-pyrrolidone moiety was introduced into the polymer chains. Second, an environmentally-friendly deoxidizer, carbohydrazide, was selected to prevent polymer oxidization by scavenging dissolved oxygen. Results showed that both the rigid groups and the deoxidizer improved the temperature resistance of the polymer and helped it maintain high viscosity under high temperature and shear rate. Using these two protection strategies, the resistant temperature of the polymer could reach 160 °C. However, the polymer network still got severely damaged at further elevated temperatures. Therefore, as the third protection strategy, the pre-added high temperature responsive crosslinking agent was applied to form new networks at elevated temperatures. The results have shown that the optimized polymer solution as a kind of fracturing fluid showed good temperature resistance up to 200 °C.

Hydrophobic associated polymer is widely used as fracturing fluids, but its cost is often higher than natural polymers. In order to reduce the cost, quaternary polymer AM/AA/NVP/MAO-12DAM (AANM) was successfully synthesized. The incorporation of N-vinyl-2-pyrrolidone (NVP) improves the temperature resistance of the polymer solution. Rheological and viscoelasticity test results showed that fluids with a lower dosage of AANM in the absence of any crosslinker had better performances than Guar gum (GG) with a crosslinker. Therefore, AANM is expected to be a more economical fracturing fluid thickener than GG.