The composite gels of konjac glucomannan (KGM) and corn starch (CS) were prepared and treated by the freeze–thaw method. For KGM–CS gels, as the starch ratio rose from 0 to 100%, storage modulus (G′) decreased by 97.7% (from 3875.69 Pa to 87.72 Pa), degradation temperature decreased from 313.32 °C to 293.95 °C, and crystallinity decreased by 16.7%. For F–KGM–CS gels, G′ decreased by 99.0% (from 20,568.10 Pa to 204.09 Pa), degradation temperature increased from 289.68 °C to 298.07 °C, and crystallinity decreased by 17.1% with more starch content. The peak in infrared spectroscopy shifted to a higher wavenumber with more starch and to a lower wavenumber by freezing the corresponding composite gels. The detected retrogradation of the composite gels appeared for KGM–CS with 80% starch and F–KGM–CS with 40% starch. The endothermic enthalpy of free water rose by 10.6% and 10.1% with the increase in starch for KGM–CS and F–KGM–CS, respectively. The results of moisture distribution found that bound water migrated to free water and the water-binding capacity reduced with more starch. The results demonstrated that the molecular interaction in composite gels was weakened by starch and strengthened by freezing.

Corn flour was prepared by wet-milling with the treatment of neutral protease and the gelatinization, thermal and rheological properties were analyzed. Tortilla was prepared with enzyme treated corn flour (ECF) and additives (xanthan gum and cassava starch) and the properties were analyzed. Compared with dry-milling corn flour (DCF) and wet-milling corn flour (WCF), the ECF had less average particle size (16.74 μm), higher peak viscosity and higher final viscosity of 2997 cP and 3300 cP, respectively. The thermal properties showed that ECF had higher ∆H and lower T_o, T_p and T_c. The G′ of ECF gel (6%, w/w) was higher than that of DCF gel and WCF gel. Dynamic viscoelastic measurement indicated that the tortillas made of ECF had lower G′ and G″ over the frequency range (0.1–100 rad/s) after adding xanthan gum and cassava starch. The gel structure of tortillas made of ECF was homogeneous in distribution of pores. The gelatinization, thermal and rheological properties of corn flour were improved by addition of neutral protease. The addition of xanthan gum and cassava starch helped to make the tortilla with porous structure and good sensory quality.

Resistant starch (RS) type 2-high-amylose corn starch (HACS) was subjected to simultaneous hydrothermal (25% moisture content, 90 °C for 12 h) and microwave (35% moisture content, 40 W/g microwaving for 4 min) treatment and zein (at a zein to treated starch ratio of 1:5, 50 °C for 1 h) to improve its resistance to enzymolysis. Scanning electron microscopy (SEM) highlighted the aggregation and adhesion of the composite. The average particle size of the composite (27.65 μm) was exceeded that of both the HACS (12.52 μm) and the hydrothermal and microwave treated HACS (hydro-micro-HACS) (12.68 μm). The X-ray diffraction results revealed that the hydro-micro-HACS and composite remained B-type, while their crystallinity significantly decreased to 16.98% and 12.11%, respectively. The viscosity of the hydro-micro-HACS and composite at 50 °C was 25.41% and 35.36% lower than that of HACS. The differential scanning calorimetry (DSC) results demonstrated that the composite displayed a new endothermic peak at 95.79 °C, while the weight loss rate and decomposition temperature were 7.61% and 2.39% lower than HACS, respectively. The RS content in HACS, the hydro-micro-HACS, and composite was 47.12%, 57.28%, and 62.74%, respectively. In conclusion, hydrothermal and microwave treatment combined with zein provide an efficient physical strategy to enhance the RS type 2-HACS.