Sol–gel silicate glasses co-doped with Gd³⁺ and Eu³⁺ ions were successfully obtained and the pronounced effect of the matrix composition on the luminescent properties and energy transfer process from Gd³⁺ to Eu³⁺ was confirmed.

This paper reports an optical investigation of Eu³⁺:PbF₂ nanocrystals distributed into silica glasses fabricated by sol–gel methods. The sample microstructure was investigated using scanning transmission electron microscopy. The β-cubic PbF₂ crystalline phase was identified using X-ray diffraction analysis. The observed emission bands correspond to ⁵D₀ → ⁷F_J (J = 0–4) transitions of Eu³⁺. The spectroscopic parameters for Eu³⁺ ions were determined based on excitation and emission measurements as well as luminescence decay analysis. Emission originating from ⁵D₀ state of Eu³⁺ ions in sample containing PbF₂ nanocrystals is long-lived in comparison to precursor sol–gel silica glasses.

In this work, the series of Tb³⁺/Eu³⁺ co-doped xerogels and derivative glass-ceramics containing CaF₂ nanocrystals were prepared and characterized. The in situ formation of fluoride crystals was verified by an X-ray diffraction technique (XRD) and transmission electron microscopy (TEM). The studies of the Tb³⁺/Eu³⁺ energy transfer (ET) process were performed based on excitation and emission spectra along with luminescence decay analysis. According to emission spectra recorded under near-ultraviolet (NUV) excitation (351 nm, ⁷F₆ → ⁵L₉ transition of Tb³⁺), the mutual coexistence of the ⁵D₄ → ⁷F_J (J = 6–3) (Tb³⁺) and the ⁵D₀ → ⁷F_J (J = 0–4) (Eu³⁺) luminescence bands was clearly observed. The co-doping also resulted in gradual shortening of a lifetime from the ⁵D₄ state of Tb³⁺ ions, and the ET efficiencies were varied from η_ET = 11.9% (Tb³⁺:Eu³⁺ = 1:0.5) to η_ET = 22.9% (Tb³⁺:Eu³⁺ = 1:2) for xerogels, and from η_ET = 25.7% (Tb³⁺:Eu³⁺ = 1:0.5) up to η_ET = 67.4% (Tb³⁺:Eu³⁺ = 1:2) for glass-ceramics. Performed decay analysis from the ⁵D₀ (Eu³⁺) and the ⁵D₄ (Tb³⁺) state revealed a correlation with the change in Tb³⁺–Eu³⁺ and Eu³⁺–Eu³⁺ interionic distances resulting from both the variable Tb³⁺:Eu³⁺ molar ratio and their partial segregation in CaF₂ nanophase.

In this article the comparisons of two new factory-made Chinese aerogel products with the Pyrogel® product, all available on the market, are presented. The aerogel products are in a flexible blanket form and all products are dedicated for high temperature applications. The properties of the samples such as their dimension stability, water vapour transmission and water absorption are also described. Additionally the microstructure and chemical composition of the products are analysed using SEM/EDS (scanning electron microscopy coupled with X-ray energy-dispersive spectroscopy). The differences in the maximum service temperature are presented. The internal self-heating of the aerogel samples is described and is compared to a similar effect observed in mineral wool samples. The results in the change of the thermal properties in a wide range of temperatures (+ 10–600°C) are shown. The obtained results are correlated with the mineral wool data. The correlation shows an advantage in a high-efficiency thermal performance of aerogel products compared to other insulation materials at high temperatures. Graphical Abstract

Optics InfoBase is the Optical Society's online library for flagship journals, partnered and copublished journals, and recent proceedings from OSA conferences.