Laser peening without coating (LPwC) involves irradiating materials covered with water with intense laser pulses to induce compressive residual stress (RS) on a surface. This results in favorable effects, such as fatigue enhancement; however, the mechanism underlying formation of the compressive RS is not fully understood. In general, tensile RS is imparted on the surface of the material due to shrinkage after heating by laser irradiation. In this study, we assessed the thermo-mechanical effect of single laser pulse irradiation and introduce a phenomenological model to predict the outcome of LPwC. To validate this model, RS distribution across the laser-irradiated spot was analyzed using X-ray diffraction with synchrotron radiation. In addition, the RS was evaluated across a line and over an area, following irradiation by multiple laser pulses with partial overlapping. Large tensile RSs were found in the spot irradiated by the single pulse; however, compressive RSs appeared around the spot. In addition, the surface RS state shifted to the compressive side due to an increase in overlap between neighboring laser pulses on the line and over the area of irradiation. The compressive RSs around a subsequent laser spot effectively compensated the tensile component on the previous spot by controlling the overlap, which may result in compressive RSs on the surface after LPwC.

In order to examine the feasibility of applying synchrotron radiation μCT imaging to alloy steels for non-destructive inspection of inclusions for potential origins of internal fatigue damage in the very high cycle region, synchrotron radiation μCT imaging was utilized for repeated non-destructive observation of Cr-Mo steel. An ultrasonic fatigue testing machine was used in aid of the repeated observation. As a result, it was found that the synchrotron radiation μCT imaging with 70 keV was useful for non-destructive observation of inclusions of more than 10 μm, one of which may be an internal fatigue origin. No identifiable damage was observed around every inclusion, and in the base metal, at least up to 70% of fatigue life was observed in the imaging volume.

Synchrotron radiation (SR) and X-ray free electron laser (XFEL) are indispensable tools not only for the exploration of science but also for the evolution of industry. We used SR and XFEL to elucidate the mechanism and the effects of laser peening without coating (LPwC) which enhances the durability of metallic materials. X-ray diffraction (XRD) employing SR revealed that the residual stress (RS) in the top surface became compressive as the laser pulse irradiation density increased with appropriate overlapping of adjacent laser pulses. SR-based computed tomography (CT) was used to nondestructively reconstruct three-dimensional (3D) images of fatigue cracks in aluminum alloy, revealing that LPwC retarded crack propagation on the surface and inside of the sample. SR-based computed laminography (CL) was applied to friction stir welded (FSWed) aluminum alloy plates to visualize fatigue cracks propagating along the welds. The fatigue crack had complicated shape; however, it became a semi-ellipsoid once projected onto a plane perpendicular to the fatigue loading direction. Ultra-fast XRD using an XFEL was conducted to investigate the dynamic response of aluminum alloy to an impulsive pressure wave simulating the LPwC condition. The diffraction pattern changed from spotty to smooth, implying grain refinement or subgrain formation. Shifts in diffraction angles were also observed, coinciding with the pressure history of laser irradiation. The durations of the dynamic phenomena were less than 1 µs; it may be possible to use high-repetition lasers at frequencies greater than kHz to reduce LPwC processing times.