Using Micro-Electro-Mechanical-Systems (MEMS) technologies, we have developed silicon wafer-based platinum microelectrode arrays (MEAs) modified with glutamate oxidase (GluOx) for electroenzymatic detection of glutamate in vivo. These MEAs were designed to have optimal spatial resolution for in vivo recordings. Selective detection of glutamate in the presence of the electroactive interferents, dopamine and ascorbic acid, was attained by deposition of polypyrrole and Nafion. The sensors responded to glutamate with a limit of detection under 1μM and a sub-1-second response time in solution. In addition to extensive in vitro characterization, the utility of these MEA glutamate biosensors was also established in vivo. In the anesthetized rat, these MEA glutamate biosensors were used for detection of cortically-evoked glutamate release in the ventral striatum. The MEA biosensors also were applied to the detection of stress-induced glutamate release in the dorsal striatum of the freely-moving rat.

We report a simple approach to the production of carbon fiber‐based amperometric microbiosensors for selective detection of hydrogen peroxide (H₂O₂), which was achieved by electrometallization of carbon fiber microelectrodes (CFMs) by electrodeposition of Pt nanoparticles. The Pt‐carbon hybrid sensing interface provided a sensitivity of 7711±587 μA ⋅ mM⁻¹ ⋅ cm⁻², a detection limit of 0.53±0.16 μM (S/N=3), a linear range of 0.8 μM–8.6 mM, and a response time of <2 sec. The morphologies of the Pt nanoparticle‐modified CFMs were characterized by scanning electron microscopy. To achieve selectivity, permseletive layers, polyphenylenediamine (PPD) and Nafion, were deposited resulting in exclusion of the anionic and cationic interferents, ascorbic acid and dopamine, respectively, at their physiologically relevant concentrations. The resultant sensors displayed a sensitivity to hydrogen peroxide of 1381±72 μA ⋅ mM⁻¹ ⋅ cm⁻², and a detection limit of 0.86±0.19 μM (S/N=3). This simple and rapid metallization method converts carbon fiber microelectrodes, which are readily accessible, to microscale Pt electrodes in 2 min, providing a platform for oxidase‐based amperometric biosensors with improved spatial resolution over more commonly used platinum electrode array microprobes.