Soluble aniline tetramer (AT) was successfully prepared by chemical oxidation method. Fourier transform infrared spectroscopy (FTIR) and ultraviolet-visible spectroscopy (UV-vis) were used to characterize its structure. The redox behavior of AT was identified through the electrochemical cyclic voltammetry studies. Then, the epoxy coating was prepared by using AT as inhibitor. Its anticorrosive property was evaluated by salt solution resistance test, polarization curve, and electrochemical impedance spectroscopy (EIS). Salt solution resistance test, polarization curves, and EIS measurements indicate that the obtained epoxy anticorrosive coating, containing 1.0% AT, exhibits remarkably enhanced corrosion protection properties on Q235 steel electrodes as compared to pure epoxy anticorrosive coating without AT. The significantly improved anticorrosion performance may be owing to the redox behavior of the AT, adsorption and inhibition effect of AT on Q235 steel surface, as well as synergistic curing effect by AT and polyamide.

The recycling of polyethylene terephthalate (PET) is the most attractive method for PET waste management because it not only decreases the load on landfill space, but also provides opportunities for reducing the use of raw petrochemical products. Therefore, in this investigation, neopentyl glycol is used for alcoholysis of waste PET, and glycolyzed PET product was applied for preparation of the waterborne alkyd resin. Furthermore, the waterborne alkyd-amino baking coatings were prepared from the waterborne alkyd based on glycolyzed waste PET and melamine formaldehyde resin and applied on tinplate. The waterborne alkyd-amino resin films showed excellent adhesion, balanced hardness and flexibility, high gloss and outstanding chemical resistance except for alkali resistance owing to hydrolysis of ester bonds.

In this paper, the waste polyethylene terephthalate (PET) was glycolysed by trimethylolpropane with zinc acetate as catalyst. The effects of different content glycolysis product of waste PET on the appearance, viscosity, particle size and molecular weight of autoxidative water-reducible alkyd resins and the corresponding film adhesion, flexibility, impact resistance, gloss, hardness and chemical resistance were studied. Meanwhile, experimental results were compared with commercial water-reducible alkyd and water-reducible alkyd without the glycolysis product of waste PET. The results show that the maximum concentration of PET in autoxidative water-reducible alkyd resins can reach 8.5 wt%, and the molecular weight, particle size and viscosity of water-reducible alkyd resin do not change much with the increase of PET concentration. The introduction of PET resulted in the viscosity of water-reducible alkyd resins being greater than that of water-reducible alkyd resin without PET; this is mainly because PET contains harder terephthalic acid monomer units. However, the particle size of water-reducible alkyd resins with waste PET is significantly lower than that of the water-reducible alkyd resin without PET; this is due to PET-free water-reducible alkyd resin containing more pentaerythritol with greater steric hindrance. In addition, the hardness of the water-reducible alkyd resin paint film (PET content is 8.5%) reaches 1H, which is higher than the hardness (HB) of the water-reducible alkyd resin paint film without PET and the commercial alkyd resin paint film, while the physical properties and chemical resistance of the former are comparable to those of the latter two kinds of paint films. Therefore, the use of waste PET in water-borne coatings systems not only reduces the cost of coatings, but also opens up a new market for recycled PET, which may contribute a promising method for management of waste PET.