Silica-supported silver nanoparticles (Ag/SiO₂) encapsulated inside the PNIPAM-based microcapsules (MC) were proved to be an efficient and easy-to-handle catalyst. Due to the hydrophilic nature of MCs, they act as microreactors in a mixed organic–aqueous environment. It was demonstrated that the catalytic activity of encapsulated Ag/SiO₂ substantially exceeds that of freely dispersed catalyst.

In the present study we report a simple and reproducible method to prepare highly ordered arrays of Fe₃O₄ superparamagnetic nanoparticles (MNPs) via block copolymer (BCP) self assembly. Pre-synthesized MNPs with a mean diameter of 6.1 nm are selectively segregated within the lamellae or hexagonally packed cylinders composed of PVP blocks in poly(styrene-b-vinylpyridine) (PS-b-PVP) block copolymers without any additional surface modification. The density of the stabilizing shell in the MNPs as well as the position of pyridine nitrogen in the PVP block of the BCPs are found to be crucial for selective incorporation of MNPs into the PVP domains. The obtained results suggest a key importance of a mutual affinity between active blocks and the nanoparticles which should be maximized in order to attain high nanoparticles loadings and long-range structural orders.

Catalytically active porous and hollow titania nanofibers encapsulating gold nanoparticles were fabricated using a combination of sol–gel chemistry and coaxial electrospinning technique. We report the fabrication of catalytically active porous and hollow titania nanofibers encapsulating gold nanoparticles (AuNPs) using a combination of sol–gel chemistry and coaxial electrospinning technique. The coaxial electrospinning involved the use of a mixture of poly(vinyl pyrrolidone) (PVP) and titania sol as the shell forming component, whereas a mixture of poly(4-vinyl pyridine) (P4VP) and pre-synthesized AuNPs constituted the core forming component. The core–shell nanofibers were calcined stepwise up to 600 °C which resulted in decomposition and removal of the organic constituents of the nanofibers. This led to the formation of porous and hollow titania nanofibers, where the catalytic AuNPs were embedded in the inner wall of the titania shell. The catalytic activity of the prepared Au@TiO₂ porous nanofibers was investigated using a model reaction of catalytic reduction of 4-nitrophenol and Congo red dye in the presence of NaBH₄. The Au@TiO₂ porous and hollow nanofibers exhibited excellent catalytic activity and recyclability, and the morphology of the nanofibers remained intact after repeated usage. The presented approach could be a promising route for immobilizing various nanosized catalysts in hollow titania supports for the design of stable catalytic systems where the added photocatalytic activity of titania could further be of significance.