Thin-film based magnetoimpedance (MI) sensors were used for quantitative determination of the concentration of magnetic nanoparticles (MNPs) in ferrogels. Ferrogels (model systems for biological tissue) were synthesized by radical polymerization of acrylamide in a stable aqueous suspension of γ-Fe₂O₃ MNPs fabricated by laser target evaporation. MI [FeNi/Ti]₃/Cu/[Ti/FeNi]₃/Ti sensitive elements were prepared by sputtering. Thorough structural and magnetic studies of MNPs, ferrogels, and multilayered sensitive element insure the complete characterization of biosensor prototype. The MI response of the sensitive element was carefully evaluated in initial state and in the presence of ferrogels with different concentration of iron oxide MNPs from 0 to 2.44 wt. %, which produced systematic changes of the MI in a frequency span of 300 kHz to 400 MHz.

The outstanding properties of selected soft magnetic materials make them successful candidates for building high performance sensors. In this paper we present our recent work regarding different sensing technologies based on the coupling of the magnetic properties of soft magnetic materials with their electric or elastic properties. In first place we report the influence on the magneto-impedance response of the thickness of Permalloy films in multilayer-sandwiched structures. An impedance change of 270% was found in the best conditions upon the application of magnetic field, with a low field sensitivity of 140%/Oe. Second, the magneto-elastic resonance of amorphous ribbons is used to demonstrate the possibility of sensitively measuring the viscosity of fluids, aimed to develop an on-line and real-time sensor capable of assessing the state of degradation of lubricant oils in machinery. A novel analysis method is shown to sensitively reveal the changes of the damping parameter of the magnetoelastic oscillations at the resonance as a function of the oil viscosity. Finally, the properties and performance of magneto-electric laminated composites of amorphous magnetic ribbons and piezoelectric polymer films are investigated, demonstrating magnetic field detection capabilities below 2.7 nT.

The microstructure and magnetic properties of sputtered permalloy films and FeNi(170 nm)/X/FeNi(170 nm) (X = Co, Fe, Gd, Gd-Co) sandwiches were studied. Laminating of the thick FeNi film with various spacers was done in order to control the magnetic softness of FeNi-based multilayers. In contrast to the Co and Fe spacers, Gd and Gd-Co magnetic spacers improved the softness of the FeNi/X/FeNi sandwiches. The magnetoimpedance responses were measured for [FeNi/Ti(6 nm)]₂/FeNi and [FeNi/Gd(2 nm)]₂/FeNi multilayers in a frequency range of 1–500 MHz: for all frequencies under consideration the highest magnetoimpedance variation was observed for [FeNi/Gd(2 nm)]₂/FeNi multilayers.