Cyanoacrylate(CA)-based tissue adhesives, although not widely used, are a feasible option to fix a mesh during abdominal hernia repair, due to its fast action and great bond strength. Their main disadvantage, toxicity, can be mitigated by increasing the length of their alkyl chain. The objective was to assess the in vitro cytotoxicity and in vivo biocompatibility in hernia repair of CAs currently used in clinical practice (Glubran(n-butyl) and Ifabond(n-hexyl)) and a longer-chain CA (OCA(n-octyl)), that has never been used in the medical field. Formaldehyde release and cytotoxicity of unpolymerized(UCAs) and polymerized CAs(PCAs) were evaluated by macroscopic visual assessment, flow cytometry and Alamar Blue assays. In the preclinical evaluation, partial defects were created in the rabbit abdominal wall and repaired by fixing polypropylene prostheses using the CAs. At 14 days post-surgery, animals were euthanized for morphology, macrophage response and cell damage analyses. Formaldehyde release was lower as the molecular weight of the monomer increased. The longest side-chain CA(OCA) showed the highest cytotoxicity in the UCA condition. However, after polymerization, was the one that showed better behavior on most occasions. In vivo, all CAs promoted optimal mesh fixation without displacements or detachments. Seroma was evident with the use of Glubran, (four of six animals: 4/6) and Ifabond (2/6), but it was reduced with the use of OCA (1/6). Significantly greater macrophage responses were observed in groups where Glubran and Ifabond were used vs. sutures and OCA. TUNEL-positive cells were significantly higher in the Glubran and OCA groups vs. the suture group. Although mild formaldehyde release occurred, OCA was the most cytotoxic during polymerization but the least once cured. The CAs promoted proper mesh fixation and have potential to replace traditional suturing techniques in hernia repair; the CAs exhibited good tissue integration and effective short-term biocompatibility, with the slightest seroma and macrophage response induced by OCA.

To determine the expression pattern of certain metalloproteinases (MMPs) known to be involved in the degradation of the extracellular matrix in cultured fibroblasts from the transversalis fascia (TF) of patients with inguinal hernia. Inguinal hernia is a common pathology, the cause of which remains unknown. It is, however, clear that the TF is one of the anatomical structures that may impede the formation of hernias, and particularly the direct type of hernia. In previous studies the authors found enhanced MMP-2 expression in TF specimens in vivo. The persistence of increased expression in cultured fibroblasts might support the idea of a genetic defect as the cause for this pathology. Fibroblasts from the TF of patients with direct and indirect inguinal hernia were cultured and compared with those obtained from control TF in terms of MMP (MMP-2 and MMP-9) expression. Significant active MMP-2 expression was shown by TF fibroblasts from young patients with direct hernias. These findings were confirmed by immunosorbent assay, immunoblotting, and zymography of the fibroblast culture media. No MMP-9 expression was detected. These results indicate that MMP-2 may be involved in the TF matrix degradative process in patients with direct hernia. The persistence of changes in MMP-2 levels in the cell cultures appears to suggest a genetic defect or irreversible change as the origin of this pathology rather than environmental factors, which may later participate in the development of the hernial process.

Background: The use of a prosthetic mesh to repair a tissue defect may produce a series of post-operative complications, among which infection is the most feared and one of the most devastating. When occurring, bacterial adherence and biofilm formation on the mesh surface affect the implant's tissue integration and host tissue regeneration, making preventive measures to control prosthetic infection a major goal of prosthetic mesh improvement. Methods: This article reviews the literature on the infection of prosthetic meshes used in hernia repair to describe the in vitro and in vivo models used to examine bacterial adherence and biofilm formation on the surface of different biomaterials. Also discussed are the prophylactic measures used to control implant infection ranging from meshes soaked in antibiotics to mesh coatings that release antimicrobial agents in a controlled manner. Results: Prosthetic architecture has a direct effect on bacterial adherence and biofilm formation. Absorbable synthetic materials are more prone to bacterial colonization than non-absorbable materials. The reported behavior of collagen biomeshes, also called xenografts, in a contaminated environment has been contradictory, and their use in this setting needs further clinical investigation. New prophylactic mesh designs include surface modifications with an anti-adhesive substance or pre-treatment with antibacterial agents or metal coatings. Conclusions: The use of polymer coatings that slowly release non-antibiotic drugs seems to be a good strategy to prevent implant contamination and reduce the onset of resistant bacterial strains. Even though the prophylactic designs described in this review are mainly focused on hernia repair meshes, these strategies can be extrapolated to other implantable devices, regardless of their design, shape or dimension.