This study evaluates the effect of CaCO₃ fillers extracted from waste eggshells on 3D-printed PLA performance. Samples of neat PLA and PLA reinforced with CaCO₃ fillers embedded with different wt.% were prepared using an FDM (fused deposition modeling) technology. The samples were examined using mechanical, dynamic mechanical, thermal, and thermal decomposition analyses. The results revealed increasing elastic moduli, tensile strength, and flexure as the filler content increased. The rheological results from the MFR tests showed that the filler content did not influence the PLA-based samples’ processability. Further, the thermal degradation of neat and various CaCO₃-wt.%-reinforced PLA specimens revealed relatively small discrepancies in their exposure to the temperature increase, mainly concerning the eggshell organic components and volatile components, from their processability up to 300 °C. By contrast, the increased filler content positively shifted the peaks along the temperature scale at the maximum degradation rate. Additionally, the weight content of the natural reinforcement strongly influenced the surface wettability and appearance of the samples. Further, the SEM analysis featured both the presence of interlayer disturbances and the interfacial compatibility the PLA with the selected fillers.

Gum rosin (GR) was used as a natural additive to improve the compatibility between polylactic acid, PLA, and poly(butylene adipate-co-terephthalate, PBAT, blended with 20 wt.% of PBAT (PLA/PBAT). The PBAT was used as a soft component to increase the ductility of PLA and its fracture toughness. The coalescence of the PBAT domains was possible due to the plasticization effect of the GR component. These domains contributed to increasing the toughness of the final material due to the variation and control of the PBAT domains’ size and consequently, reducing the stress concentration points. The GR was used in contents of 5, 10, 15, and 20 phr. Consequently, the flexural properties were improved and the impact resistance increased up to 80% in PLA/PBAT_15GR with respect to the PLA/PBAT formulation. Field emission scanning electron microscope (FESEM) images allowed observing that the size of PBAT domains of 2–3 µm was optimal to reduce the impact stress. Differential scanning calorimetry (DSC) analysis showed a reduction of up to 8 °C on the PLA melting temperature and up to 5.3 °C of the PLA glass transition temperature in the PLA/PBAT_20GR formulation, which indicates an improvement in the processability of PLA. Finally, transparent films with improved oxygen barrier performance and increased hydrophobicity were obtained suggesting the potential interest of these blends for the food packaging industry.

Multi-layered glass and carbon-reinforced polymer composites may exhibit unique properties comparatively with the benchmark, proven they are being tailored bounded by several requirements. The paper herein approaches issues on the influence of the various contents and orientation of UD carbon fibre constitutive on the mechanical, dynamical and thermal expansion if embedded along with glass fibres in different stacking sequencing within an unsaturated polymer resin. The results show that the architectures with the highest content of carbon fibres (e.g. GF:CF(60:40) – 0° and 90°) provide the best tensile and flexural properties, and behave better under dynamical loading conditions and temperature variations, no matter the orientation directions. In addition, it was shown that a thorough understanding can be attained, with respect to the UD carbon fibre content, and different orientations influence on the overall composite material properties, taking into account the data retrieved from dynamical and thermal expansion runs.

The contribution aims to bring forth a novel synthesis route in developing transparent UV LED-curable coatings accounting for various exposure options. A selection of perfluoropolyether (PFPE)-urethane methacrylate and acrylate resins, free-radical photo-initiator Omnirad 2100, and two distinct silane-based crosslinking agents were blended under a weight ratio of 75:20:5 (without crosslinker) and 70:15:5:10, respectively. The coatings were cured under a UV LED 4 × 3 matrix light emitting source, in a chamber under a controlled atmosphere, by means of an in-house developed conveyor belt type platform, at different conveyor belt speeds (5, 50, 150, 250, and 500 mm/s). The morphologies of fabricated coatings were characterized by FTIR revealing high conversion rates (e.g., from 98 to 100%) for increased exposure time as a result of the 5 or 50 mm/s values, on all combinations. Dynamic–mechanical and optical properties of UV LED-cured transparent coatings were also investigated. A negative shift of the glass transition temperature values with a decrease in exposure time, in all combinations, from about 60 °C to 30 °C, along with storage moduli lowering in the glassy plateau further favors higher exposure times for curing. The refractive indices of poly-mers were from 1.38 to 1.40, whereas the thermo-optic coefficients are showing minor changes around the value of 2.55∙10⁻⁴ K⁻¹.