The present paper reports on the results of some experiments dealing with the recycling of mixed cathode ray tube (CRT) glass waste in the production of high-strength mortars. Waste CRT glass cullet was previously milled, and sieved, and the only fine fraction was added to the fresh mortar in order to replace part of the natural aggregate. The addition of superplasticizer was also investigated. All hydrated materials displayed high compressive strength after curing. Samples containing CRT mixed glass showed a more rapid increase of strength with respect to the reference compositions, and materials with a superplasticizer content of 1% showed the best overall performance due to the favourable influence of the small glass particles which increase the amount of silicate hydrated produced. The induced coupled plasma (ICP) analysis made on the solutions, obtained from the leaching tests, confirmed the low elution of hazardous elements from the monolithic materials produced and consequently their possible environmental compatibility.