The processing techniques, microstructural characteristics, and erosion corrosion behaviour of Cr₃C₂–NiCr and tungsten carbide (WC)-based cermet coatings are reviewed in this work. Conventional and nanocrystalline Cr₃C₂–NiCr and WC-based cermet coatings are generally synthesized using thermal spray technique. The wear, erosion, and corrosion protection ability of conventional and nanocermet coatings are compared based on available literature. In Cr₃C₂–NiCr coatings, the corrosion resistance is offered by NiCr metal matrix while the wear resistance is provided by the carbide ceramic phase, making it suitable for erosion–corrosion protection. The nanocrystalline cermet coatings exhibits better erosion–corrosion resistance as compared to the conventional coatings. The nanocrystalline coatings reduces the erosion–corrosion rate significantly compared to conventional coatings. It is attributed to the presence of the protective NiCr metallic binder that allows easier and faster re-passivation when the coating is subjected to wear and the fine-grain structure with homogeneous distribution of the skeleton network of hard carbide phases. In addition, corrosion-accelerated erosion dominates the reaction mechanism of erosion–corrosion and, therefore, higher hardness, strength, and better wear resistance of nanocermet coating along with its faster repassivation kinetics accounts for improved corrosion resistance as compared to conventional coatings.

Cr₃C₂–NiCr coatings have been used extensively to combat the erosion corrosion of hydro power turbine blades made of stainless steel. Cr₃C₂–NiCr coatings are also used in aqueous corrosive environments due to the high corrosion resistance rendered by the NiCr binder. In this investigation, both erosion and corrosion environments are introduced to cermet coating to study corrosion behavior using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) techniques. The cermet coatings are useful for reducing the risk of deterioration of mechanical properties of hydro power turbines due to the continuous exposure to the erosive and corrosive action of the corrosive environment containing silt. It was observed that Cr₃C₂–NiCr coating offered a reasonable improvement in corrosion resistance when compared to bare substrate. The corrosion behavior of the coating was studied in a 150 mL solution of 0.1 M NaCl with 2 gms of quartz particles (0.2–0.8 mm) at various rotation speeds (3000, 4500, 6000 rpm) of the solution over a 1 h immersion using potentiodynamic polarization and EIS studies in a specifically designed experimental set-up for erosion corrosion. When compared to the bare stainless steel samples at 3000 rpm and 6000 rpm, the coating showed the highest improvement at 6.57 times and the least improvement at 3.79 times, respectively.