In this study, we present a facile, one-step method for the manufacturing of all-cellulose, layered membranes containing cellulose nanocrystals (CNC), TEMPO (2,2,6,6-tetramethylpiperidine-1-oxyl radical)-mediated oxidized cellulose nanofibers (TO-CNF), or zwitterionic polymer grafted cellulose nanocrystals (CNC-g-PCysMA) as functional entities in combination with cellulose fibers and commercial grade microfibrillated cellulose. The presence of active sites such as hydroxyl, carbonyl, thioethers, and amines, gave the membranes high adsorption capacities for the metal ions Au (III), Co (II), and Fe (III), as well as the cationic organic dye methylene blue (MB). Furthermore, the membranes served as excellent metal-free catalysts for the decolorization of dyes via hydrogenation. A 3-fold increase of the hydrogenation efficiency for cationic dyes such as rhodamine B (RhB) and methylene blue was obtained in the presence of membranes compared to NaBH4 alone. Water-based processing, the abundance of the component materials, and the multifunctional characteristics of the membranes ensure their potential as excellent candidates for water purification systems.

We report (1) successful extraction and characterization of cellulose from northern hemisphere green macroalgae Ulva lactuca (Ulva fenestrata) collected along the Swedish west coast and cultivated indoors under controlled conditions, followed by (2) its utilization in the production of lignin-free cellulose nanofibrils (CNF). Cellulose was extracted by sequential treatment with ethanol, hydrogen peroxide, sodium hydroxide, and hydrochloric acid, yielding a cellulose-rich insoluble fraction. The extracted cellulose was disintegrated into CNF using a mechanical homogenization process without any further enzymatic pre-treatments. In addition, regenerated cellulose was prepared. XRD characterization of the CNF showed characteristic peaks for the cellulose I allomorph and confirmed that the nanofibrils were semicrystalline with a crystallinity index of 48%. Regenerated cellulose was mostly amorphous with an XRD pattern indicating the presence of the cellulose II allomorph. The cellulose fractions were essentially free from inorganic substances and thermally stable up to around 260 °C. Structural mapping with CP-MAS ¹³C-NMR sustains the cellulose content of CNF and regenerated cellulose, respectively, yet ion chromatography identified the presence of 10–15% xylose in the fractions. Optotracing was used as a novel and non-disruptive tool to selectively assess the polysaccharide composition of the cellulose fractions and produced CNF aiming to shed light on this hitherto non-resolved origin of xylose in Ulva cell wall matter. Fluorescence excitation and emission spectra of a panel of 4 oligothiophenes identified and verified the presence of cellulose and sustain the conclusion that the isolated fractions consist of cellulose intertwined with a small amount of a xylose-containing glucan copolymer. Graphic

The cell wall polysaccharide ulvan was isolated from two species of the seaweed Ulva collected along the Swedish west coast. Acidic extraction was benchmarked against hot water extraction with enzymatic purification and against commercial ulvan. Extracted ulvan contained 11-18 % g/g of ash, some protein (up to 1.3 % g N/g) but minimal colored impurities. The ulvans had high molecular weights (660,000-760,000 g/mol) and were composed of 77-79 % g/g carbohydrates, mainly rhamnose, xylose, glucose, glucuronic acid, and iduronic acid. The extraction protocol and the ulvan source strongly impact the molecular weight and the chemical composition. Acidic extraction caused almost complete desulfation of the isolated ulvan while the other method preserved a significant degree of SO3 substituents. Elemental analysis of ash remaining after thermal degradation showed presence of common mineral elements such as Na, Ca, Mg, Al, and K, but none of the heavy metals Pb, Hg, or As.

Hydrogels based on the polysaccharide ulvan from the green macroalgae Ulva fenestrata were synthesized and evaluated as an adsorbent for heavy metals ions and methylene blue. Ulvan was extracted from Ulva fenestrata using diluted hydrochloric acid and recovered by precipitation with EtOH. The extracted ulvan was converted into ulvan dialdehyde via periodate-oxidation and subsequently combined with gelatin yielding hydrogels. The hydrogels showed good water-uptake capacity with a maximum swelling degree of 2400 % in water and 900 % in PBS buffer. Adsorption tests of methylene blue showed a maximum adsorption capacity of 465 mg/g. The adsorption data of methylene blue followed the pseudo-second order kinetics and agreed with the Langmuir adsorption isotherm. The maximum adsorption capacity of heavy metal ions was 14 mg/g for Cu²⁺, 7 mg/g for Co²⁺and 6 mg/g for Ni²⁺and Zn²⁺ indicating that the hydrogels have a stronger affinity for Cu²⁺ than for Co²⁺, Ni²⁺, and Zn²⁺.