Acrylamide with a double bond and amide group can not only copolymerize with macromolecules of crumb rubber but also react with acidic groups in asphalt, so it was selected as a modifier to activate crumb rubber through chemical graft action. The purpose is to improve the compatibility between crumb rubber and asphalt and thus improve the rheological properties and storage stability of rubber asphalt. Infrared spectroscopy (IR) and scanning electron microscopy (SEM) were used to characterize the crumb rubbers and their modified asphalt. It was found that the crumb rubber of grafting acrylamide had better compatibility in asphalt due to its larger specific surface area and chemical reaction with asphalt. In addition, the high temperature rheological test, low temperature creep test, and polymer separation test were carried out to study the effect of grafted activated crumb rubber on the properties of modified asphalt. The results showed that compared with modified asphalt with common crumb rubber (CRMA), the rheological properties and storage stability of modified asphalt with grafting activated crumb rubber (A–G–R) were improved significantly. The results of microscopic and macroscopic tests show that the activated rubber particles have a larger contact area with asphalt due to a rougher surface and the chemical cross-linking between rubber particles and asphalt further strengthens their interaction. Therefore, there is a relatively stable blend system formed in modified asphalt, and its performance of modified asphalt has been improved.

According to the theory of molecular design, crumb rubber was grafting activated with acrylamide and then used as asphalt binder modifier. An orthogonal three-factor, three-level test was designed to optimize the preparation process of modified asphalt. Softening point, viscosity, rutting factor, ductility, stiffness modulus and creep speed index were selected as evaluation indicators to study the effects of rubber content, shear time and shear temperature by variance analysis and range analysis. The results show that the rubber content had a significant impact on the performance of modified asphalt with grafting-activated crumb rubber, while the shear temperature and shear time had little effect. The grafting activated crumb rubber content of 20%, shear temperature of 170–190 °C, and shear time of 90 min was determined as the reasonable preparation process. Modified asphalt with common crumb rubber (CRMA) and modified asphalt with grafting activated crumb rubber (A-G-R) were prepared, respectively, using the reasonable process to analyze the influence of grafting activation of crumb rubber. The results indicate that A-G-R had smaller softening point difference, lower segregation index and more stable and uniform dispersed phase.