Titanium alloys are widely used in various fields, but their machinability is poor because the chip would easily adhere to the tool surface during cutting, causing poor surface quality and tool wear. To improve the cutting performance of titanium alloy Ti-6Al-4V, experiments were conducted to investigate the effect of micro textured tool on the cutting performances. The cemented carbide tools whose rake faces were machined with line, rhombic, and sinusoidal groove textures with 10% area occupancy rates were adopted as the cutting tools. The effects of cutting depth and cutting speed on feed force and main cutting force were discussed based on experimental results. The results show that the cutting force produced by textured tools is less than that produced by non-textured tools. Under different cutting parameters, the best cutting performance can be obtained by using sinusoidal textured tools among the four types of tools. The wear of micro textured tools is significantly lower than that of non-textured tools, due to a continuous lubrication film between the chip and the rake face of the tool that can be produced because the micro texture can store and replenish lubricant. The surface roughness obtained using the textured tool is better than that using the non-textured tool. The surface roughness Ra can be reduced by 35.89% when using sinusoidal textured tools. This study is helpful for further improving the cutting performance of cemented carbide tools on titanium alloy and prolonging tool life.

Three kinds of grooved textures with different geometric patterns were prepared on cemented carbide tool surfaces. Finite element software FLUENT was used to simulate and analyse the fluid pressure of lubricants on the different micro-groove textured surfaces. Friction and wear experiments of titanium alloy balls and cemented carbides were carried out to investigate the tribological properties. The results show that the friction coefficient of the line groove textured surface is the smallest under dry friction conditions. Moreover, the friction coefficient of the sinusoidal groove textured surface is the smallest under fluid lubricated conditions. Experimental results show that lubrication of the grooved textured surfaces is consistent with the numerical simulation results. The main friction reduction mechanism of textures involves reducing the contact area of friction pairs and capturing debris under unlubricated conditions and supplying lubrication to form a continuous lubrication film and producing a dynamic pressure effect under fluid lubricated conditions.

Surface texturing has become a potential method to obtain a low friction coefficient under dry/lubricated conditions for different mechanical product surfaces. The mechanism of friction and wear reduction from a micro-texture on the surface of cemented carbide cutting tools was investigated by dry cutting a titanium alloy. Three kinds of micro-textures, namely, line, sinusoidal and rhombic grooves, with different area occupancy rates were produced by a laser on the cemented carbide surface. Experiments and finite element simulation of ABAQUS were used to investigate the tribological characteristics of micro-textured cemented carbide. The results indicated that the line-textured cemented carbide with an area occupancy rate of 10% showed a low friction coefficient of 0.076, which is approximately 34% of the non-textured sample. Few adhesives appeared on the textured surface, while a large number of adhesives were attached to the smooth surface after 30 min of dry friction between the cemented carbide and the titanium alloy balls. Moreover, among the three textures, the line-groove texture has the smallest friction coefficient and a good anti-wear effect. The results show that the existence of a groove texture can effectively reserve the wear debris, reduce the bond wear and weaken the furrow effect.

To further study the discharge characteristics and machining mechanism of micro-electrical discharge machining (micro-EDM), the variation trends of the discharge energy and discharge crater size with actual discharge duration are discussed based on single-pulse experiments. The polarity effect of micro-EDM was analyzed according to the motion characteristics of electrons and ions in the discharge plasma channel. The results show that the discharge current and voltage of micro-EDM were independent of the discharge width and open-circuit voltage. The energy utilization rate of the short-pulse discharge was relatively high, and the energy utilization rate decreased gradually as the discharge duration increased. Even if the mass of the positive ion was much larger than that of the electron, the kinetic energy of the positive ion was still less than that of the electron when bombarding the surface of the electrode. The acceleration and speed of electrons were very high, and the number of times that electrons bombarded the surface of positive electrode was more than 600 times that of positive ions bombarding the surface of the negative electrode during the same time.