Polyurethane chemistry can yield diverse sets of polymeric materials exhibiting a wide range of properties for various applications and market segments. Utilizing lignin as a polyol presents an opportunity to incorporate a currently underutilized renewable aromatic polymer into these products. In this work, we will review the current state of technology for utilizing lignin as a polyol replacement in different polyurethane products. This will include a discussion of lignin structure, diversity, and modification during chemical pulping and cellulosic biofuels processes, approaches for lignin extraction, recovery, fractionation, and modification/functionalization. We will discuss the potential of incorporation of lignins into polyurethane products that include rigid and flexible foams, adhesives, coatings, and elastomers. Finally, we will discuss challenges in incorporating lignin in polyurethane formulations, potential solutions and approaches that have been taken to resolve those issues.

In this study, a biobased phenolic adhesive was successfully developed by entirely substituting both petroleum-based phenol and formaldehyde with an unmodified corn stover biorefinery lignin and glyoxal (a biobased dialdehyde), respectively. Lignin-glyoxal resins were synthesized using an alkaline catalyst with a molar ratio of lignin to glyoxal of 1:2. Chemical, thermal, and mechanical properties of the lignin, lignin-based resins, and final adhesives were assessed following appropriate standard test methods. The analysis of lignins and lignin-based resin molar mass was performed using gel permeation chromatography. The lignin-glyoxal resin was found to have a 3-fold higher average molecular weight than the starting lignin, demonstrating the successful integration of lignin into the polymeric resin network. The curing of the formulated adhesives was studied using differential scanning calorimetry and dynamic mechanical analysis. Although the lignin-glyoxal resin had a higher curing temperature (167 °C) than a conventional phenol-formaldehyde resin (142 °C) and the formulated lignin-formaldehyde resin (146 °C), the rate and degree of cure were similar or better than the other two resins. The adhesion strengths of the formulated adhesives were determined using single-lap-joint veneer samples cured according to recommended press parameters for commercial adhesives. The lignin-glyoxal adhesive had a relatively high dry adhesion strength (3.9 MPa), with over 90% wood failure, but failed the wet adhesion test (boiling water test). Although the formulated lignin-glyoxal adhesive failed the boiling water test, it had excellent stability at room temperature water, remaining intact after 1 week during the water immersion test. The high dry adhesion strength makes this class of lignin-based formaldehyde-free adhesives a unique biobased glue for the production of interior grade plywood and oriented strand boards.

Background: Pretreatment is a critical step in the conversion of lignocellulose to fermentable sugars. Although many pretreatment processes are currently under investigation, none of them are entirely satisfactory in regard to effectiveness, cost, or environmental impact. The use of hydrogen peroxide at pH 11.5 (alkaline hydrogen peroxide (AHP)) was shown by Gould and coworkers to be an effective pretreatment of grass stovers and other plant materials in the context of animal nutrition and ethanol production. Our earlier experiments indicated that AHP performed well when compared against two other alkaline pretreatments. Here, we explored several key parameters to test the potential of AHP for further improvement relevant to lignocellulosic ethanol production. Results: The effects of biomass loading, hydrogen peroxide loading, residence time, and pH control were tested in combination with subsequent digestion with a commercial enzyme preparation, optimized mixtures of four commercial enzymes, or optimized synthetic mixtures of pure enzymes. AHP pretreatment was performed at room temperature (23°C) and atmospheric pressure, and after AHP pretreatment the biomass was neutralized with HCl but not washed before enzyme digestion. Standard enzyme digestion conditions were 0.2% glucan loading, 15 mg protein/g glucan, and 48 h digestion at 50°C. Higher pretreatment biomass loadings (10% to 20%) gave higher monomeric glucose (Glc) and xylose (Xyl) yields than the 2% loading used in earlier studies. An H₂O₂ loading of 0.25 g/g biomass was almost as effective as 0.5 g/g, but 0.125 g/g was significantly less effective. Optimized mixtures of four commercial enzymes substantially increased post-AHP-pretreatment enzymatic hydrolysis yields at all H₂O₂ concentrations compared to any single commercial enzyme. At a pretreatment biomass loading of 10% and an H₂O₂ loading of 0.5 g/g biomass, an optimized commercial mixture at total protein loadings of 8 or 15 mg/g glucan gave monomeric Glc yields of 83% or 95%, respectively. Yields of Glc and Xyl after pretreatment at a low hydrogen peroxide loading (0.125 g H₂O₂/g biomass) could be improved by extending the pretreatment residence time to 48 h and readjusting the pH to 11.5 every 6 h during the pretreatment. A Glc yield of 77% was obtained using a pretreatment of 15% biomass loading, 0.125 g H₂O₂/g biomass, and 48 h with pH adjustment, followed by digestion with an optimized commercial enzyme mixture at an enzyme loading of 15 mg protein/g glucan. Conclusions: Alkaline peroxide is an effective pretreatment for corn stover. Particular advantages are the use of reagents with low environmental impact and avoidance of special reaction chambers. Reasonable yields of monomeric Glc can be obtained at an H₂O₂ concentration one-quarter of that used in previous AHP research. Additional improvements in the AHP process, such as peroxide stabilization, peroxide recycling, and improved pH control, could lead to further improvements in AHP pretreatment.

Background: For cellulosic biofuels processes, suitable characterization of the lignin remaining within the cell wall and correlation of quantified properties of lignin to cell wall polysaccharide enzymatic deconstruction is underrepresented in the literature. This is particularly true for grasses which represent a number of promising bioenergy feedstocks where quantification of grass lignins is particularly problematic due to the high fraction of p- hydroxycinnamates. The main focus of this work is to use grasses with a diverse range of lignin properties, and applying multiple lignin characterization platforms, attempt to correlate the differences in these lignin properties to the susceptibility to alkaline hydrogen peroxide (AHP) pretreatment and subsequent enzymatic deconstruction. Results: We were able to determine that the enzymatic hydrolysis of cellulose to to glucose (i.e. digestibility) of four grasses with relatively diverse lignin phenotypes could be correlated to total lignin content and the content of p-hydroxycinnamates, while S/G ratios did not appear to contribute to the enzymatic digestibility or delignification. The lignins of the brown midrib corn stovers tested were significantly more condensed than a typical commercial corn stover and a significant finding was that pretreatment with alkaline hydrogen peroxide increases the fraction of lignins involved in condensed linkages from 88–95% to ~99% for all the corn stovers tested, which is much more than has been reported in the literature for other pretreatments. This indicates significant scission of β-O-4 bonds by pretreatment and/or induction of lignin condensation reactions. The S/G ratios in grasses determined by analytical pyrolysis are significantly lower than values obtained using either thioacidolysis or 2DHSQC NMR due to presumed interference by ferulates. Conclusions: It was found that grass cell wall polysaccharide hydrolysis by cellulolytic enzymes for grasses exhibiting a diversity of lignin structures and compositions could be linked to quantifiable changes in the composition of the cell wall and properties of the lignin including apparent content of the p-hydroxycinnamates while the limitations of S/G estimation in grasses is highlighted.

Aromatic monomer yields from lignin depolymerization can be predicted using quantifiable lignin properties.