Effect of hydrofluoric acid surface treatments on micro-shear bond strength of CAD/CAM ceramics

The aim of this study was to compare the discoloration potential of calcium-enriched mixture (CEM) cement, white mineral trioxide aggregate (WMTA) and calcium hydroxide (CH), after placement in pulp chamber. Access cavities were prepared in 40 intact maxillary central incisors. Then, a 2×2 mm box was prepared on the middle third of the inner surface on the buccal wall of the access cavity. The specimens were randomly assigned into four groups; the boxes in the control group were left empty, in groups 1 to 3, the boxes were filled with CH, WMTA and CEM cement, respectively. The access cavities and the apical openings were sealed using resin modified glass ionomer (RMGI). The color measurement was performed with a spectrophotometer at the following intervals: before (T0), immediately after placement of the filling material (T1), one week (T2), 1 month (T3), 3 months (T4) and 5 months (T5) after filling of the box and finally immediately after removing the material from the boxes (T6). Color change (ΔE) values were calculated using the sample Kolmogorov-Smirnov test to determine the normal distribution of data, followed by ANOVA, repeated measured ANOVA and post-hoc Tukey’s tests. All materials led to clinically perceptible crown discoloration after 1 week. The highest ΔE value belonged to WMTA group. Discoloration induced by CEM cement was not significantly different from CH or the control group (P>0.05). CEM cement may be the material of choice in the esthetic region, specifically pertaining to its lower color changing potential compared to WMTA.

Jafari Z, et al. Restor Dent Endod. 2018 Apr;43:e27. https://doi.org/10.5395/rde.2018.43.e27

SUMMARY: Objective: Computer aided design-computer aided machining (CAD-CAM) ceramic crowns are replacing ceramo-metal ones due to newly developed mechanical properties and esthetics. To obtain knowledge about their interactions due to polishing and occlusal contacts with the opposing dental enamel specimen, including surface roughness and wear, the three-body wear simulation was investigated. Methods and Materials: The surface roughness (RA) and wear rate (mm) of four CAD-CAM blocks with different compositions including Vita Mark II, e.max, Suprinity, and Enamic, after two surface treatments of glazing and polishing, and their opposing enamel specimens, were investigated using a mastication simulator and atomic force microscope. Results: The roughness of all ceramic and to a greater extent enamel samples, with the exception of enamel opposing polished Enamic samples, was decreased after wear. No significant difference in wear was evident for the ceramic samples between the glazed and polished treatments. Lower wear rates were recorded only for polished Vita Mark II and polished Enamic in comparison to the glazed ones. Conclusion: The newly developed polishing systems for CAD-CAM ceramics can be good alternatives to reglazing, because the roughness and wear rate of both the ceramic and the opposing enamel will either not change or decrease.

56 Introduction: The aim of this study was to compare the micro-shear bond strength of composite resin on superficial and deep dentin after conditioning with phosphoric acid and Erbium-Doped Yttrium Aluminum Garnet (Er:YAG) laser. Methods: Thirty human molars were selected, roots were removed and crowns were bisected to provide a total of 60 half-crowns. Specimens were ground to expose superficial and deep dentin. Samples were assigned to six groups: (1) AS (acid etching of superficial dentin); (2) AD (acid etching of deep dentin); (3) LS (Er:YAG laser irradiation on superficial dentin); (4) LD (Er:YAG laser irradiation on deep dentin); (5) LAS (Er:YAG laser irradiation on superficial dentin followed by acid etching); (6) LAD (Er:YAG laser irradiation on deep dentin followed by acid etching) The adhesive protocol was performed. Samples were thermocycled and micro-shear bond strength was tested to failure. The data were submitted to statistical analysis with one-way analysis of variance (ANOVA) and Tukey post hoc test. Results: The AS group, demonstrated the greatest amount of micro-shear bond strength. Statistical analysis showed a decrease in bond strength in laser-treated groups which was more significant for deep dentin. Conclusion: Preparation of dentin with laser did not improve bonding to superficial and deep dentin.