Biomimetic sensor technology is always superior to existing human technologies. The scorpion, especially the forest scorpion, has a unique ability to detect subtle vibrations, which is attributed to the microcrack-shaped slit sensillum on its legs. Here, the biological sensing mechanism of the typical scorpion (Heterometrus petersii) was intensively studied in order to newly design and significantly improve the flexible strain sensors. Benefiting from the easy-crack property of polystyrene (PS) and using the solvent-induced swelling as well as double template transferring method, regular and controllable microcrack arrays were successfully fabricated on top of polydimethylsiloxane (PDMS). Using this method, any physical damage to PDMS could be effectively avoided. More fortunately, this bio-inspired crack arrays fabricated in this work also had a radial-like pattern similar to the slit sensillum of the scorpion, which was another unexpected imitation. The gauge factor (GF) of the sensor was conservatively evaluated at 5888.89 upon 2% strain and the response time was 297 ms. Afterward, it was demonstrated that the bio-inspired regular microcrack arrays could also significantly enhance the performance of traditional strain sensors, especially in terms of the sensitivity and response time. The practical applications, such as the detection of human motions and surface folding, were also tested in this work, with the results showing significant potential applications in numerous fields. This work changes the traditional waste cracks on some damaged products into valuable things for ultrasensitive mechanical sensors. Moreover, with this manufacturing technique, we could easily realize the simple, low cost and large-scale fabrication of advanced bioinpired sensors.

In this study, titanium alloy (Ti-4Al-1.5Mn), magnesium alloy (Mg-Li9-A3-Zn3), or aluminum alloy (Al7075-T6) were used to construct the shell model of helicopter rotor blade to study the solid particle erosion of helicopter rotor blades. The erosion resistance of the three materials at different angles of attack (6°, 3°, or 0°) and particle collision speeds (70, 150, or 220 m/s) was examined using the finite volume method, the discrete phase method, and erosion models. In addition, the leading edge of the helicopter blades was coated with two types of bionic anti-erosion coating layers (V- and VC-type), in an attempt to improve erosion resistance at the angles of attack and particle collision speeds given above. The results showed that Ti-4Al-1.5Mn had the best erosion resistance at high speed, followed by Al7075-T6 and Mg-Li9-A3-Zn3. The angle of attack appeared to affect only the surface area of the blade erosion, while the erosion rate was not affected. Finally, the results of this article showed that the V-type bionic coating had better erosion resistance than the VC-type coating at the same impact speeds. The angle of attack did not have a significant effect on the erosion rate of the bionic coating.