This study focuses on the relationship between the complexity of pore structure and capillary water absorption of concrete, as well as the connection behavior of concrete in specific directions. In this paper, the water absorption of concrete with different binders was tested during the curing process, and the pore structure of concrete was investigated by mercury intrusion porosimetry (MIP). The results show that the water absorption of concrete with mineral admixtures is lower, mainly due to the existence of reasonable pore structure. The effect of slag on concrete modification is more remarkable comparing with fly ash. In addition, the analysis shows that the pore with different diameters has different fractal characteristics. The connectivity probability and water absorption of unidirectional chaotic pore are linearly correlated with the pore diameter of 50–550 nm, and the correlation coefficient reaches a very significant level, and detailed analysis was undertaken to interpret these results based on fractal theory.

Nano-sized C-S-H, a promising early strength agent, can accelerate the hydration rate of Portland cement and increase the early compressive strength of cement-based composites effectively. Nano-sized C-S-H suspensions with different contents of effective constituent and size distributions were prepared by a convenient coprecipitation method and the microstructures were analyzed by Zeta potential, XRD and FT-IR. The exothermic heat, early mechanical properties, hydration degree and hydration products of cement with/without nano-sized C-S-H cured at different temperatures were studied by hydration exothermic, XRD, SEM and TG analysis. Nano-sized C-S-H with semi-crystalline structures was prepared, and the size of the nano-sized C-S-H seeds showed an obvious increase with an increase in theoretical concentration, and slight precipitation in the suspension was observed when the theoretical concentration was 2%. The XRD, TG and SEM analyses showed that nano-sized C-S-H expedites the reaction of C₃S in the first 24 h; therefore, the hydration induction period is obviously shortened. The 8 h, 16 h and 24 h compressive strength of mortars containing nano-sized C-S-H increased by 176.0%, 145.6% and 43.9%, respectively, compared with the reference mortar. The enhancement effects of nano-sized C-S-H at 10 °C were lower than that at 20 °C.

The use of tricyclic copolymer latex (AMPS) can effectively improve the carbonation resistance of sulphoaluminate cement. This paper investigated polymer AMPS and polycarboxylic acid to modify sulphoaluminate cement materials by exploring the carbonation level of sulphoaluminate cement paste and mortar and the strength before and after carbonation. Then, the optimal dosage of polymer and polycarboxylic acid was obtained so that the carbonation resistance of sulphoaluminate cement reached the best state. The compressive strength was significantly improved by adding AMPS for sulphoaluminate cement paste and mortar. After carbonation, the strength decreased and combined with the carbonation level; it was concluded that the carbonation resistance of sulphoaluminate cement materials was the best when the optimal dosage of AMPS and polycarboxylic acid was 5% and 1.8%, respectively. Due to the addition of AMPS, the hydrated calcium aluminosilicate (C-A-S-H) and hydrated calcium silicate (C-S-H) gels, generated by the hydration of sulphoaluminate cement and the surface of unreacted cement particles, are wrapped by AMPS particles. The water is discharged through cement hydration. The polymer particles on the surface of the hydration product merge into a continuous film, which binds the cement hydration product together to form an overall network structure, penetrating the entire cement hydration phase and forming a polymer cement mortar with excellent structural sealing performance. To prevent the entry of CO₂ and achieve the effect of anti-carbonation, adding polycarboxylic acid mainly improves the sample’s internal density to achieve the anti-carbonation purpose.