The effects of complex well conditions in shale oil wells on the swelling and tribological properties of high-acrylonitrile stator rubber used in screw pumps were investigated in this study. Tests were conducted considering the combined effects of immersion medium, temperature, and duration. The key parameters measured included mass change rate, volume change rate, hardness, elongation at break, tensile strength, surface micro-morphology of the rubber after thermal expansion and swelling, friction coefficient, and wear quantity. The results indicated that in the actual well fluids, the mass change rate of high-acrylonitrile rubber ranged from −1.08% to 1.29%, with a maximum volume change rate of 2.78%. In diesel oil, the greatest mass change rate of the rubber was 4.68%, and the volume change rate did not exceed ±1%, indicating superior swelling resistance. In both actual well fluids and diesel oil, the maximum decreases in hardness were 8.7% and 9.5%, respectively. Tensile strength and elongation at break decreased with increasing immersion temperature, with elongation at break in 80 °C diesel oil decreasing by over 50%, indicating a significant decline in the tensile properties of the rubber. The average friction coefficient of rubber specimens immersed in actual well fluids at three temperatures, as well as in diesel oil at 25 and 50 °C, decreased compared with the high-acrylonitrile rubber without thermal expansion and swelling. However, the average friction coefficient of rubber specimens immersed in diesel oil at 80 °C increased. The wear quantity of the rubber increased following immersion in both media. Additionally, the friction coefficient and wear quantity of the rubber increased with increasing immersion temperatures. The results of the study can offer valuable insights into assessing the durability of properties in high-acrylonitrile stator rubber under complex well conditions.

Plunger pumps are widely used in oil pumping units around the world. The water content of the wellbore is increasing along with the development progress, so the lubricating capacity of the well fluids between the plunger and barrel is decreasing correspondingly. Commonly, the substrate material of the plunger and barrel are stainless steel, and the plunger surface is usually covered with nickel-based coating. Therefore, the performance of the plunger and barrel has been affected due to poor lubrication and eccentric wear. Non-smooth surfaces have been proven to improve the tribology performance in many cases. A surface texturing plunger covered with specific dimples has been prepared by using laser surface texturing technology. The morphology of the surface texturing plunger was characterized and analyzed. The tribology performance of surface texturing plunger samples was tested using standard friction and wear test machines with oil and water lubrication, respectively. The results indicated that surface texturing could effectively reduce the coefficient of friction, and the wear resistance of the surface textured samples has been improved to some extent.

A theoretical model for the micro-texture on the inner wall of the stator rubber in screw pumps was developed. The finite element analysis method was employed. The pressure and streamline distributions for warhead-type, concentric circle-type, and multilayer rectangular-type textured surfaces were calculated. The effects of textured morphology, groove depth, groove width, and other parameters on the lubrication field were systematically investigated and analyzed. A nanosecond laser was employed to process the textured rubber surface of the stator in the screw pump. Subsequently, a micro-texture friction performance test was conducted on the rubber surface of the stator in actual complex well fluids from shale oil wells. Given the results of the simulation analysis and experimental tests, the lubrication characteristics of textured rubber surfaces with varying texture morphologies, rotational speeds, and mating loads were revealed. Furthermore, it indicated that the irregular symmetric warhead-type micro-texture exhibited excellent dynamic pressure lubrication performance compared with concentric circle-type and multilayer rectangular-type textures. The irregular symmetry enhanced the dynamic pressure lubrication effect, enhanced the additional net load-bearing capacity of the oil film surface, and reduced friction. As the groove depth increased, the volume and number of vortices within the groove also increased. The fluid kinetic energy was transformed into vortex energy, leading to a reduction in wall stress on the surface of the oil film, thereby affecting its bearing capacity. Initially, the maximum pressure on the wall surface of the oil film increased and then decreased. The optimal dynamic pressure lubrication effect was achieved with a warhead-type texture size of 3 mm, a groove width of 0.2 mm, and a groove depth of 0.1 mm. Well-designed texture morphology and depth parameters significantly enhanced the oil film-bearing capacity of the stator rubber surface, improving the dynamic pressure lubrication effect, and consequently extending the service life of the stator–rotor interface in the screw pump.

This paper develops a composite weaving structure, combining hexagonal micro-bumps and hexagonal grooves, in the design of the rubber surface of the screw pump. This allows us to solve the problem of high torque and fast wear of the rubber stator during the operation of screw pump lifting oil recovery, based on the bionic hexagonal surface structure, traditional surface damping principle, and fluid dynamic pressure lubrication theory. Finite element analysis is first conducted to quantitatively analyze the impacts of the parallel side distance, groove width, and groove depth on the surface flow field and wall pressure field of the composite hexagonal structure. Based on the simulation law, the rubber surface laser structure is then designed and prepared by nanosecond laser processing. Afterward, tribological experiments are conducted under the condition of long-term immersion in the actual extraction fluid of shale oil wells. This aims at simulating the actual downhole oil production conditions and quantitatively studying the impact of the size of the composite hexagonal structure on the lubrication characteristics of the friction part of the stationary rotor, as well as the effect of abrasion reduction. The results show that, within the simulation range, the smaller the parallel side distance, the higher the load-carrying capacity. In addition, the hexagonal weave with a parallel side distance of 3 mm has a higher wall load carrying capacity than that with distances of 4 mm and 5 mm. When the groove width is equal to 0.4 mm, the oil film load carrying capacity is higher than that in the case of 0.2 mm. When the groove depth increases, the oil film pressure first increases and then stabilizes or decreases after reaching 0.3 mm. In the hexagonal weave, the friction ratio of the rotor is equal to 0.4 mm. In the tribological experiment of hexagonal weave, the smaller the parallel side distance, the smaller the friction coefficient, and the 0.5 mm weave has the highest performance.

The dissolvable bridge plug is one of the most important tools for multi-stage hydraulic fracturing in the field of oil/gas development. The plug provides zonal isolation to realize staged stimulation and, after fracturing, the plug is fully dissolved in produced liquids. A bionic surface was introduced to improve the performance of the plug. Surface dimples in the micron dimension were prepared on the dissolvable materials of the plug. The experimental results showed that the surface dimples changed the hydrophilic and hydrophobic properties of the dissolvable materials. The dissolution rate has a great relation with the parameters of the dimples and can be controlled by choosing the dimples’ parameters to some degree.