Well-defined, semi-degradable polyester/polymethacrylate block copolymers, based on ε-caprolactone (CL), d,l-lactide (DLLA), glycolide (GA) and N,N′-dimethylaminoethyl methacrylate (DMAEMA), were synthesized by ring-opening polymerization (ROP) and atom transfer radical polymerization. Comprehensive degradation studies of poly(ε-caprolactone)-block-poly(N,N′-dimethylaminoethyl methacrylate) (PCL-b-PDMAEMA) on hydrolytic degradation and enzymatic degradation were performed, and those results were compared with the corresponding aliphatic polyester (PCL). The solution pH did not affect the hydrolytic degradation rate of PCL (a 3% M_n loss after six weeks). The presence of a PDMAEMA component in the copolymer chain increased the hydrolysis rates and depended on the solution pH, as PCL-b-PDMAEMA degraded faster in an acidic environment (36% M_n loss determined) than in a slightly alkaline environment (27% M_n loss). Enzymatic degradation of PCL-b-PDMAEMA, poly(d,l-lactide)-block-poly(N,N′-dimethylaminoethyl methacrylate) (PLA-b-PDMAEMA) and poly(lactide-co-glycolide-co-ε-caprolactone)-block-poly(N,N′-dimethylaminoethyl methacrylate) (PLGC-b-PDMAEMA) and the corresponding aliphatic polyesters (PCL, PLA and PLGC) was performed by Novozyme 435. In enzymatic degradation, PLGC degraded almost completely after eleven days. For polyester-b-PDMAEMA copolymers, enzymatic degradation primarily involved the ester bonds in PDMAEMA side chains, and the rate of polyester degradation decreased with the increase in the chain length of PDMAEMA. Amphiphilic copolymers might be used for biomaterials with long-term or midterm applications such as nanoscale drug delivery systems with tunable degradation kinetics.

In this study, the phase transition phenomena of linear poly(acrylic acid) (PAA) and linear or star-shaped poly(acrylic acid-co-methyl acrylate) (P(AA-co-MA)) in highly concentrated KCl solutions were investigated. The effects of polymer molecular weight, topology, and composition on their phase transition behavior in solution were investigated. The cloud point temperature (T_CP) of polymers drastically increased as the KCl concentration (C_KCl) and solution pH increased. C_KCl strongly influenced the temperature range at which the phase transition of PAA occurred: C_KCl of 1.0–2.2 M allowed the phase transition to occur between 30 and 75 °C. Unfortunately, at C_KCl above 2.6 M, the T_CP of PAA was too high to theoretically trigger the crystallization of KCl. The addition of hydrophobic methyl acrylate moieties decreased the T_CP into a temperature region where KCl crystallization could occur. Additionally, the hydrodynamic diameters (D_h) and zeta potentials of commercial PAA samples were examined at room temperature and at their T_CP using dynamic light scattering. The salt concentration (from 1 to 3 M) did not impact the hydrodynamic diameter of the molecules. D_h values were 1500 and 15 nm at room temperature and at T_CP, respectively.

The presented drug delivery polymeric systems (DDS), i.e., conjugates and self-assemblies, based on grafted and star-shaped polymethacrylates have been studied for the last few years in our group. This minireview is focused on the relationship of polymer structure to drug conjugation/entrapment efficiency and release capability. Both graft and linear polymers containing trimethylammonium groups showed the ability to release the pharmaceutical anions by ionic exchange, but in aqueous solution they were also self-assembled into nanoparticles with encapsulated nonionic drugs. Star-shaped polymers functionalized with ionizable amine/carboxylic groups were investigated for drug conjugation via ketimine/amide linkers. However, only the conjugates of polybases were water-soluble, giving opportunity for release studies, whereas the self-assembling polyacidic stars were encapsulated with the model drugs. Depending on the type of drug loading in the polymer matrix, their release rates were ordered as follows: Physical ≥ ionic > covalent. The studies indicated that the well-defined ionic polymethacrylates, including poly(ionic liquid)s, are advantageous for designing macromolecular carriers due to the variety of structural parameters, which are efficient for tuning of drug loading and release behavior in respect to the specific drug interactions.

Synthesis, physicochemical characterization, and the enzymatic degradation of the amphiphilic miktoarm star-shaped polymers is reported herein. First, star-shaped macroinitiators, based on N,N′-dimethylaminoethyl methacrylate (DMAEMA) and glycerol dimethacrylate (GDMA) ((PDMAEMA)_n-PGDMA), were synthesized. Due to the presence of hydroxyl groups in the macroinitiator core, polyesters such as poly(ɛ-caprolactone) (P(ɛ-CL)), polylactide (PLA) and poly(lactide-co-glycolide) (PLGA) were synthesized using ring opening polymerization (ROP). Comprehensive degradation studies on enzymatic degradation, using a lipase from Pseudomonas cepacia, were performed. Enzymatic degradation was monitored by weight measurements and nuclear magnetic resonance spectroscopy (¹H NMR). The fastest degradation rate was observed for the polymer with the lowest molecular weight. Amphiphilic miktopolymers may find application as biomaterials for long- or mid-term period drug-delivery systems.

We report a one-pot synthesis of well-defined A₅B and A₈B miktoarm star-shaped polymers where N,N-dimethylaminoethyl methacrylate (DMAEMA) and various cyclic esters such as ε-caprolactone (ε-CL), lactide (LA) and glycolide (GA) were used for the synthesis. Miktopolymers were obtained by simultaneously carrying out atom transfer radical polymerization (ATRP) of DMAEMA, ring-opening polymerization (ROP) of cyclic esters, and click reaction between the azide group in gluconamide-based (GLBr₅-Az) or lactonamide-based (GLBr₈-Az) ATRP initiators and 4-pentyn-1-ol. The relatively low dispersity indices of the obtained miktoarm stars (Đ = 1.2–1.6) indicate that control over the polymerization processes was sustained despite almost complete monomers conversions (83–99%). The presence of salts from phosphate-buffered saline (PBS) in polymer solutions affects the phase transition, increasing cloud point temperatures (T_CP) values. The critical aggregation concentration (CAC) values increased with a decreasing number of average molecular weights of the hydrophobic fraction. Hydrolytic degradation studies revealed that the highest reduction of molecular weight was observed for polymers with PCL and PLGCL arm. The influence of the composition on the miktopolymers hydrophilicity was investigated via water contact angle (WCA) measurement. Thermogravimetric analysis (TGA) disclosed that the number of arms and their composition in the miktopolymer affects its weight loss under the influence of temperature.

Polymers are becoming a very popular tool in the crystallization of different compounds. In this work, a new method of crystallization is proposed using stimuli-responsive star polymer in order to obtain hollow structure crystals. In these experiments, amphiphilic copolymer of acrylic acid (AA) and methyl acrylate (MA) were used for isohydric crystallization via they cooling of KCl in deionized water solution. The experiments were realized in quartz cuvette with a magnetic stirrer using a specialized spectrometer with precise temperature control. The crystallization course was monitored by the absorbance readings and analysis of the nucleation energetic effect. It was proved that the moment of the polymer’s phase transition occurrence had an important role in the crystal growth process. On the other hand, the occurrence of phase transition did not trigger the nucleation. The supercoolings achieved in the presence of the polymer were significantly higher compared to pure salt crystallization. On the basis of analysis of Particle Size Distribution (PSD) and Critical Aggregation Concentration (CAC) of the polymer, it was proposed that the hydrophobic particles of macromolecules created from polymeric aggregates served as templates for the formation of hollow crystals. Their purity was verified using thermogravimetric analysis (TGA), 1H NMR, and XRD. Only trace amounts of polymer were found in the crystalline product.