A pure ferrite and epoxy samples as well as the epoxy/ferrite composites with different 20 wt.%, 30 wt.%, 40 wt.%, and 50 wt.% weight ferrite contents have been prepared by the chemical co-precipitation method. AC-conductivity and dielectric properties such as the dielectric constant and dielectric loss of the prepared samples have been studied. The obtained results showed that the samples had a semiconductor behavior. The dielectric constant of the composites has been calculated theoretically using several models. For the composite sample that contains 20 wt.% of ferrites, these models give satisfactory compliance, while for the composite samples with a higher percentage of nanofillers, more than 30 wt.% theoretical results do not coincide with experimental data. The investigated polymer has very low conductivity, so this type of polymer can be useful for high-frequency applications, which can reduce the losses caused by eddy current. Thus, the prepared samples are promising materials for practical use as elements of microwave devices.

Increase in the spontaneous magnetization up to x < 0.5 is a sequence of appearance of the additional magnetic moment of 2 μ_B of the Ni²⁺ cations in tetrahedral positions. For x > 0.5, the moment decreases in octahedral positions and the spontaneous magnetization also decreases.

Nanostructured NiFe film was obtained on silicon with a thin gold sublayer via pulsed electrodeposition and annealed at a temperature from 100 to 400 °C in order to study the effect of heat treatment on the surface microstructure and mechanical properties. High-resolution atomic force microscopy made it possible to trace stepwise evolving microstructure under the influence of heat treatment. It was found that NiFe film grains undergo coalescence twice—at ~100 and ~300 °C—in the process of a gradual increase in grain size. The mechanical properties of the Au/NiFe nanostructured system have been investigated by nanoindentation at two various indentation depths, 10 and 50 nm. The results showed the opposite effect of heat treatment on the mechanical properties in the near-surface layer and in the material volume. Surface homogenization in combination with oxidation activation leads to abnormal strengthening and hardening-up of the near-surface layer. At the same time, a nonlinear decrease in hardness and Young’s modulus with increasing temperature of heat treatment characterizes the internal volume of nanostructured NiFe. An explanation of this phenomenon was found in the complex effect of changing the ratio of grain volume/grain boundaries and increasing the concentration of thermally activated diffuse gold atoms from the sublayer to the NiFe film.