Interpenetrating polymer network (IPN) hydrogels are crosslinked by two or more polymer networks, providing free volume space in the three-dimensional network structure, and providing conditions for the sustained and controlled release of drugs.

Hemorrhea is one of the major problems in war, trauma care, and surgical operation that threaten the life of the injured and patients. As a novel polymeric hemostatic agent, biodegradable chitosan can stop bleeding through a variety of approaches. In this paper, chitosan with various molecular parameters was prepared from chitin as raw material through deacetylation, oxidative degradation, hydrophilic modification, and salt formation reactions. The influence of different polymer parameters on the hemostatic effects of chitosan was investigated by in vitro coagulation time and dynamic coagulation assay. The results showed that when the molecular weights were high (10⁵–10⁶) and approximate, the coagulation effect of chitosan improved with a decrease of the deacetylation degree and achieved a prominent level in a moderate degree of deacetylation (68.36%). With the same degree of deacetylation, the higher the molecular weight of chitosan, the better the procoagulant effect. The substituent derivatives and acid salts of chitosan showed significant procoagulant effects, especially the acid salts of chitosan. In addition, the hemostasis mechanism of chitosan with various parameters was preliminarily explored by analyzing the plasma recalcification time (PRT). The efforts in this paper laid a basis for further study of the structure–activity relationship and the mechanism of chitosan hemostasis.

Burns are physically debilitating and potentially fatal injuries. Two marine biomaterials, carboxymethyl chitosan (CMC) and collagen peptides (COP), have emerged as promising burn dressings. In this paper, sponges of carboxymethyl chitosan grafted with collagen peptide (CMC–COP) were prepared by covalent coupling and freeze drying. Scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectroscopy were then used to characterize the prepared sponges. To evaluate the wound healing activity of the CMC–COP sponges, in vitro tests including cell viability scratch wound healing and scald wound healing experiments were performed in rabbits. Appearance studies revealed the porous nature of sponges and FTIR spectroscopy demonstrated the successful incorporation of COP into CMC. The in vitro scratch assay showed that treatment with CMC–COP sponges (at 100 μg/mL) had significant effects on scratch closure. For burn wounds treated with CMC–COP, regeneration of the epidermis and collagen fiber deposition was observed on day 7, with complete healing of the epidermis and wound on days 14 and 21, respectively. Based on the pathological examination by hematoxylin and eosinstaining, the CMC–COP group demonstrated pronounced wound healing efficiencies. These results confirmed that the CMC–COP treatment enhanced cell migration and promoted skin regeneration, thereby highlighting the potential application of these sponges in burn care.

Considering the great harm to the human body caused by severe and massive bleeding, in this study, chitosan-grafted norfloxacin (CTS-NF) composites were prepared with chitosan (CTS) and norfloxacin (NF) as raw materials by a 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide-mediated coupling method to solve the limitations of slow hemostatic and poor anti-infective effects of current dressings on the market. The effects of the mass ratio of CTS to NF (M_CTS/M_NF), reaction temperature T and reaction time t on the grafting rate (η%) of the products were investigated through single factor tests. The preparation process was optimized with the η% as an evaluation index by means of the Box–Behnken test design and response surface analysis. The antimicrobial activity was evaluated by inhibition zone assay, and the hemostatic activity of the prepared composites was evaluated in vitro and in vivo. The results suggested that the optimum preparation conditions were the mass ratio of CTS to NF (M_CTS/M_NF) 5:3, reaction temperature 65 °C, and reaction time 4 h. Under this condition, the η% of CTS-NF was 45.5%. The CTS-NF composites displayed significant antimicrobial activities. Moreover, in vitro hemostasis results revealed that the CTS-NF composite had a lower blood clotting index and absorbed red blood cells to promote aggregation. In vivo ear and live hemostasis, the CTS-NF groups showed short hemostatic time (49.75 ± 3.32 s and 50.00 ± 7.21 s) and more blood loss (0.07 ± 0.010 g and 0.075 ± 0.013 g). The results showed that CTS-NF reduced the bleeding time and volume, exhibiting a significant coagulation effect. Therefore, the CTS-NF sponge is expected to be a new, effective hemostatic and antibacterial material in the future.