Zinc oxide nanoparticles (ZnO NPs) are known for their antibacterial, antioxidant, and anti-inflammatory activities. Moreover, ZnO NPs can stimulate cell migration, re-epithelialization, and angiogenesis. All these attributes are highly relevant to wound healing. Local administration of ZnO NPs to the wound can be achieved through electrospun nanofibers. We hypothesized that the use of poly(lactide-co-glycolic acid) (PLGA)/silk fibroin (SF) nanofiber-based delivery of ZnO would maintain the bioavailability of NPs on the wound area and synchronization with the unique structural features of electrospun nanofibers, could stimulate wound closure, re-epithelialization, collagen deposition, cellular migration, and angiogenesis. In this study, we fabricated PLGA/SF (PS) nanofibrous (NF) membranes with and without ZnO NPs and extensively characterized them for various physicochemical and biological attributes. Scanning electron microscopy (SEM) revealed smooth fibers and ZnO concentration-dependent increase in the fiber diameter. Transmission electron microscopy (TEM) also confirmed the encapsulation of ZnO NPs in the polymer matrix. The successful loading of ZnO was further confirmed by X-ray diffraction. Furthermore, mechanical testing revealed a ZnO concentration-dependent increase in the tensile strength. Moreover, biocompatibility was evaluated through in vitro cell culture. A mild anti-oxidant activity was also noted mainly due to the presence of silk fibroin. In vitro antibacterial tests revealed a ZnO concentration-dependent increase in antibacterial activity and PLGA/SF/3% ZnO (PSZ3) remained completely active against E. coli and S. aureus. More importantly, NF membranes were evaluated for their in vivo wound healing potential. The PSZ3 NF membrane not only facilitated the early wound closure but also remarkably enhanced the quality of wound healing confirmed through histopathological analysis. Re-epithelialization, granulation tissue formation, collagen deposition, and angiogenesis are some of the key parameters significantly boosted by ZnO loaded composite NF membranes. Based on extensive characterization and biological evaluation, the PSZ3 NF membrane has turned out to be a potential candidate for wound healing applications.

Diabetic wound (DW) healing is a major clinical challenge due to multifactorial complications leading to prolonged inflammation. Electrospun nanofibrous (NF) membranes, due to special structural features, are promising biomaterials capable to promote DW healing through the delivery of active agents in a controlled manner. Herein, we report a multifunctional composite NF membrane loaded with ZnO nanoparticles (NP) and oregano essential oil (OEO), employing a new loading strategy, capable to sustainedly co-deliver bioactive agents. Physicochemical characterization revealed the successful fabrication of loaded nanofibers with strong in vitro anti-bacterial and anti-oxidant activities. Furthermore, in vivo wound healing confirmed the potential of bioactive NF membranes in epithelialization and granulation tissue formation. The angiogenesis was greatly prompted by the bioactive NF membranes through expression of vascular endothelial growth factor (VEGF). Moreover, the proposed NF membrane successfully terminated the inflammatory cycle by downregulating the pro-inflammatory cytokines interleukin −6 (IL-6) and matrix metalloproteinases-9 (MMP-9). In vitro and in vivo studies revealed the proposed NF membrane is a promising dressing material for the healing of DW.

Vascularization and bone regeneration are two closely related processes during bone reconstruction. A three-dimensional (3D) scaffold with porous architecture provides a suitable microenvironment for vascular growth and bone formation. Here, we present a simple and general strategy to construct a nanofibrous poly(l-lactide)/poly(ε-caprolactone) (PLLA/PCL) scaffold with interconnected perfusable microchannel networks (IPMs) based on 3D printing technology by combining the phase separation and sacrificial template methods. The regular and customizable microchannel patterns within the scaffolds (spacings: 0.4 mm, 0.5 mm, and 0.6 mm; diameters: 0.8 mm, 1 mm, and 1.2 mm) were made to investigate the effect of microchannel structure on angiogenesis and osteogenesis. The results of subcutaneous embedding experiment showed that 0.5/0.8-IPMs (spacing/diameter = 0.5/0.8) and 0.5/1-IPMs (spacing/diameter = 0.5/1) scaffolds exhibited more vascular network formation as compared with other counterparts. After loading with vascular endothelial growth factor (VEGF), VEGF@IPMs-0.5/0.8 scaffold prompted better human umbilical vein endothelial cells (HUVECs) migration and neo-blood vessel formation, as determined by Transwell migration, scratch wound healing, and chorioallantoic membrane (CAM) assays. Furthermore, the microangiography and rat cranial bone defects experiments demonstrated that VEGF@IPMs-0.5/0.8 scaffold exhibited better performance in vascular network formation and new bone formation compared to VEGF@IPMs-0.5/1 scaffold. In summary, our results suggested that the microchannel structure within the scaffolds could be tailored by an adjustable caramel-based template strategy, and the combination of interconnected perfusion microchannel networks and angiogenic factors could significantly enhance vascularization and bone regeneration.