Today, as a result of the advancement of technology and increasing environmental problems, the need for clean energy has considerably increased. In this regard, hydrogen, which is a clean and sustainable energy carrier with high energy density, is among the well-regarded and effective means to deliver and store energy, and can also be used for environmental remediation purposes. Renewable hydrogen energy carriers can successfully substitute fossil fuels and decrease carbon dioxide (CO₂) emissions and reduce the rate of global warming. Hydrogen generation from sustainable solar energy and water sources is an environmentally friendly resolution for growing global energy demands. Among various solar hydrogen production routes, semiconductor-based photocatalysis seems a promising scheme that is mainly performed using two kinds of homogeneous and heterogeneous methods, of which the latter is more advantageous. During semiconductor-based heterogeneous photocatalysis, a solid material is stimulated by exposure to light and generates an electron–hole pair that subsequently takes part in redox reactions leading to hydrogen production. This review paper tries to thoroughly introduce and discuss various semiconductor-based photocatalysis processes for environmental remediation with a specific focus on heterojunction semiconductors with the hope that it will pave the way for new designs with higher performance to protect the environment.

Hydroxyapatite and bioactive glass particles were added to pure magnesium and an AZ91 magnesium alloy and then consolidated into disc-shaped samples at room temperature using high-pressure torsion (HPT). The bioactive particles appeared well-dispersed in the metal matrix after multiple turns of HPT. Full consolidation was attained using pure magnesium, but the center of the AZ91 disc failed to fully consolidate even after 50 turns. The magnesium-hydroxyapatite composite displayed an ultimate tensile strength above 150 MPa, high cell viability, and a decreasing rate of corrosion during immersion in Hank’s solution. The composites produced with bioactive glass particles exhibited the formation of calcium phosphate after 2 h of immersion in Hank’s solution and there was rapid corrosion in these materials.