It was found that mesoporous graphite carbon nitride (mpg-C₃N₄) prepared using melamine as precursor and ammonium chloride as bubble template, has good photocatalytic activity under visible light irradiation. In order to improve the photocatalytic performance of mpg-C₃N₄, it was combined with metal-organic frameworks ZIF-8. Taking tetracycline hydrochloric acid (TC) solution as a model pollutant, the photocatalytic activity of composites was studied to select the optimal composite ratio and pH value. Moreover, the initial concentration of hydrogen peroxide and active oxidation species were also investigated. The results showed that when the loading of ZIF-8 is 40 wt%, the removal efficiency was the best and 74.8% of TC can be removed. The degradation efficiency of TC was negatively affected under extreme pH conditions, but the composite photocatalyst mpg-C₃N₄-ZIF-8 has a relatively higher degradation efficiency on TC at mild pH value (4–8). The removal efficiency was the best at pH 8, and 75.1% of TC can be removed, in which the adsorption capacity was 430.7 mg·g⁻¹ and the photodegradation capacity was 548.6 mg·g⁻¹. The order of active species affecting the photocatalytic degradation of TC by mpg-C₃N₄-ZIF-8 was hole > superoxide radical > hydroxyl radical.