Fabricating an Inconel 718 superalloy using electromagnetic stirring assisted laser solid forming (EMS-LSF) is a novel method to modify its microstructure and mechanical properties by consuming the Nb element in the γ phase to alleviate interdendritic segregation. The precipitate of the δ phase at 950 °C after EMS-LSF can help to achieve the uniform diffusion of Nb, and can also improve its mechanical properties. The precipitation behavior of the δ phase in an EMS-LSF Inconel 718 superalloy with different heat treatment processes has been investigated. The results show that the morphology of the δ phase changes from rod-like to a long-needle shape and tends to grow from the inter dendrite to the core dendrite with electromagnetic field intensity increasing, which is accompanied by the “cutting” and “dissolution” of the Laves phase. Through precipitation kinetics analysis, the precipitation rate of the δ phase is seen to increase with the electromagnetic field intensity increasing. Under a combination of electromagnetic stirring and laser solid forming, the microhardness of the Inconel 718 samples increased slightly due to the fact that a higher content of Nb was distributed in the core dendrite resulting from the serious convection of liquid metal, which can strengthen the matrix.

Laser forming repair (LFR) technology has considerable potential in high strength steel structure repair. 34CrNiMo6 steel has been widely used in high-value components, and it is imperative to repair these damaged components. In this study, two different thicknesses of repaired layers are deposited on the 34CrNiMo6 wrought substrate with five layers and 20 layers via LFR technology. The microstructure, phases, microhardness, and tribological properties are analyzed using optical microscopy, scanning electron microscopy, X-ray diffraction, Vickers hardness testing, and dry sliding wear testing. These results show that the 34CrNiMo6 repaired layers were successfully deposited on the substrate. The microstructure of the laser-repaired layers in the five-layer sample included bainite and retained austenite. For the 20-layer sample, the microstructure in the top of the repaired layers was still bainite and retained austenite, whereas that in the bottom of the repaired layers was transformed into ferrite and cementite. The average coefficients of friction of repaired layers is not significantly different from the substrate. The wear rate of the five LFR layers, 20-layer LFR, and substrate samples were 12.89 × 10⁻⁶, 15 × 10⁻⁶, and 23.87 × 10⁻⁶ mm³/N·m, respectively. The laser forming repaired samples had better wear resistance compared to the substrate. The wear mechanism of laser forming repaired samples is abrasive wear; whereas that of the substrate is abrasive wear and fatigue wear.

Alloy sheets of type 2060 aluminum–lithium were welded by laser beam welding (LBW) filled with ER2319 Al-5.6Cu wire. Microstructural observations showed the uneven distribution of columnar grains, equiaxed grains and equiaxed dendrite grains in the weld. The θ′(Al₂Cu) phase and other phases precipitated in the weld. The θ′(Al₂Cu) phase centrally distributed at the grain boundaries. During the immersion corrosion, the pitting corrosion first occurred and then gradually expanded and transformed to intergranular corrosion and exfoliation corrosion. The electrochemical corrosion test showed a higher corrosion tendency of the base metal and heat-affected zone for the lower corrosion potential, but the corrosion current density of the weld was relatively larger. The segregation of Cu, Mg and other elements at the grain boundary aggravated the occurrence of intergranular corrosion.