In the present study, nickel phosphorous alloys (Ni-P) and Ni-P/ silicon carbide (SiC) nanocomposite coatings were deposited by electrodeposition on steel substrates in order for their microstructural properties to be assessed while using SEM, XRD, and three-dimensional (3D) profilometry as well as nanoindentation. The amorphisation of the as-plated coatings was observed in all cases, whereas subsequent heat treatment induced crystallization and Ni3P intermetallic phase precipitation. Examination of the surface topology revealed that the surface roughness follows the deposition characteristics and heat treatment induced microstructural changes. Additionally, substantial improvements in mechanical properties, including hardness, yield stress, and elasticity modulus, were obtained for the Ni-P, Ni-P/SiC nanocomposites when heat treated as seen from the nanoindentation results. A Finite Element Analysis (FEA) was developed to simulate the nanoindentation tests that enable the precise extraction of the Ni-P and Ni-P/SiC nanocomposite coatings’ stress-strain behavior. It is shown that the correlation between the nanoindentation tests and the computational models was satisfactory, while the stress-strain curves revealed higher yield points for the heat-treated samples.

Selective laser melting is one of the additive manufacturing technologies that have been known for building various and complicated shapes. Despite numerous advantages of additive manufacturing technologies, they strongly influence the microstructure and typically show a relatively high surface roughness. In this study, maraging steel was produced by selective laser melting (SLM), and its microstructure, hardness and corrosion behavior before and after heat treatment were studied and compared to traditionally manufactured ones (wrought, forged samples). In addition, the effect of electropolishing on the surface roughness was evaluated. The microstructural study was carried out by scanning electron microscopy equipped with electron backscattered diffraction in three different sections: parallel to the top surface (xy), transverse cross section (xz) and longitudinal cross section (yz). The same characterization was applied to heat-treated samples, austenitized and quenched as well as the aged ones. The results showed that selective laser melting produced a fine grain martensitic structure (in the as-printed condition) with a surface roughness (R_a) of about 10 µm. There was no sign of preferred texture or anisotropy in the microstructure of as-print SLM materials. The SLM microstructure was similar in all 3 sections (xy, xz and yz). Despite finer microstructure, nano-hardness and corrosion behavior of SLM and conventional wrought maraging steel in heat-treated conditions were similar. Aging resulted in the maximum nano-hardness and the minimum corrosion potential values. Precipitation has the main role in both hardness and corrosion behavior. Electropolishing was optimized and reduced the surface roughness (R_a) by 65%.

In this study, electrodeposition of NiP composite coatings with the addition of SiC 100 nm was carried out on low carbon steel studying the effect of additives (sodium dodecyl sulfate, saccharin), particles load (10 or 20 g/L) and current density (1, 2 and 4 A/dm²). As a benchmark, coatings from an additive-free bath were also deposited, despite additives being essential for a good quality of the coatings. The coating’s morphology and composition were evaluated by scanning electron microscope (SEM) equipped with energy dispersive spectroscopy (EDS). It was shown that by addition of sodium dodecyl sulfate (SDS), pure NiP coating with a higher P content was achieved, and their morphology changed to nodular. SDS also reduced the codeposited fraction of SiC particles, while saccharin increased it. SiC loading and current density had less impact respect to the additives on codeposition of SiC particles. Finally, the microhardness of NiP coatings did not increase linearly by codeposition of SiC particles.

This study aimed to deposit high entropy alloy (HEA) coatings with five different elements, Ni, Co, Cu, Mo, and W, from a single aqueous bath. The influence of pH, current density, and complex agent on the composition of deposited coating was examined. It was shown that Mo and W were codeposited mainly with Ni and Co. pH had the most impact on the codeposition of reluctant elements like Mo and W, while current density had the minimum effect. The deposited coating had a metallic, dense, and nodular morphology with configurational entropy of around 1.6 R.

NiP (P > 10 wt.%) coatings are amorphous coatings whose structure can be transformed by heat treatment into a crystalline structure and hardened by precipitation of Ni₃P. In this study, NiP coatings and composite ones with SiC nanoparticles were produced by electrodeposition, and their structural transformation by heat treatment was studied using differential scanning calorimetry (DSC) and X-ray diffraction (XRD). The microhardness and the scratch and corrosion resistance of the coatings were evaluated and compared before and after different heat treatments. The results showed that in as-plated condition, the addition of SiC particles in the coatings did not modify the microstructure, microhardness, or electrochemical behavior. However, the SiC particles’ role was disclosed in combination with heat treatment. Composite coatings that were heat treated at 300 °C had higher microhardness and scratch resistance than the pure NiP one. In addition, composite coatings maintained their scratch resistance up to 400 °C, while in the case of the NiP ones, there was a reduction in scratch resistance by heating at 400 °C. It was also concluded that heating temperature has the main role in hardness and corrosion resistance of NiP and composite coatings, rather than heating time. The optimum heat-treatment protocol was found to be heating at 360 °C for 2 h, which resulted in a maximum microhardness of about 1500 HV_0.02 for NiP and its composite coating without sacrificing the corrosion resistance.