The compressive and flexural strengths of mortars modified with ethylene-vinyl acetate (EVA) were experimentally investigated for use in three-dimensional (3D) additive construction (3DAC). EVA powder, which is available in a premix type, was employed as an admixture. The test results for the cast specimens showed that, at a curing age of 28 days, the compressive strengths ranged from 32.92 MPa to 43.50 MPa, and the flexural strengths ranged from 12.73 MPa to 14.49 MPa. The compressive and flexural strengths of the printed specimens were relatively lower: 23% to 26% and 3% to 7%, respectively. The compressive strength also decreased and the flexural strength increased when the EVA/cement ratio was increased. The results of the experiment reveal that the EVA-modified mortar had a high rate of strength development early on, making the material advantageous for use in 3DAC. It was determined that the appropriate EVA/cement ratio ranged between 5% and 15%. However, the printed specimens exhibited lower compressive and flexural strengths than did the cast specimens, and the compressive strength decreased as the EVA content was increased. This study provides the compressive and flexural strengths of common EVA-modified mortars, important data for 3DAC applications.

The primary purpose of this study was to investigate the feasibility of applying polymeric cementitious materials to three-dimensional additive construction (3DAC). Specifically, styrene–butadiene rubber (SBR) latex was employed as an admixture to produce SBR-modified cementitious mixtures, and their fresh properties were experimentally investigated to determine the feasibility of their use in the 3DAC process. The SBR/cement ratio was controlled based on four main materials (i.e., cement, sand, silica fume, and fly ash) in order to determine the optimal fresh properties. The test results revealed that the SBR-modified cementitious mixtures showed excellent flowability, extrudability, buildability, and open time, all of which are required for 3DAC materials. The optimal flow of the SBR-modified cementitious mixtures was 70% ± 1%, which is appropriate for 3DAC applications. According to the experiment results, the SBR-modified cementitious mixtures were sufficiently competitive to serve as a new class of materials for 3D additive construction.

The properties of normal cementitious mixtures currently employed to the construction projects cannot be used to the three-dimensional concrete printing technology. This study experimentally investigated the compressive and flexural strength development of styrene-butadiene rubber (SBR)-modified cementitious mixtures for use as basic three-dimensional concrete printing (3DCP) materials. The SBR/cement ratio was a variable of the mix proportion used to produce cast and printed specimens. Experiments were conducted using these specimens to determine the compressive and flexural strength levels of the SBR-modified cementitious mixtures. The results indicated that the compressive strengths of the SBR-modified cementitious mixtures proposed in this study were never less than those of existing 3D concrete printing materials previously introduced for 3DCP applications. It was confirmed that the addition of SBR latex effectively improved the strength of the cementitious mixtures because the relative compressive and flexural strengths increased with increases in the SBR/cement ratio. Moreover, the higher early (i.e., 1-day) strength indicates that the SBR-modified cementitious mixtures would be advantageous to the 3DCP process. However, the compressive and flexural strengths of the printed specimens were weaker than those of the cast specimens.

Ensuring an appropriate casting time window is of great importance for achieving desired quality and performance of aging materials. In this paper, the effects of promoter and cross-linking agent on the working life—the period a mixture stays in a workable condition—of low-temperature-cured acrylic polymer concrete (PC) are investigated in order to develop mixture proportions that can be effectively applied in cold weather conditions. The experimental variables included in this study are: (1) curing temperatures (−20, −10 and 0 °C); (2) N,N-dimethyl-p-toluidine (DMT) contents (0.5, 1.0, 1.5 and 2.0 phr (parts per hundred parts of resin)); and (3) trimethylolpropane trimethacrylate (TMPTMA) contents (0, 2.5 and 5 phr). Results indicated a strong relevance between binder’s setting time and PC’s working life. Additionally, it was observed that the working life of acrylic PC was substantially shortened as the curing temperature and contents of DMT and TMPTMA increased. Results of a two-way analysis of variance (ANOVA) revealed that TMPTMA had a greater impact on the working life than DMT. Finally, this study developed an equation that can be used to estimate PC working life, based on the binder’s setting time. The findings of this study will be used as valuable information for cold weather applications of acrylic PC.

In this study, the fresh properties of ethylene–vinyl acetate (EVA)-modified cementitious mixtures were experimentally investigated to evaluate the feasibility of this type of material being used in additive construction by extrusion (ACE). The EVA/cement ratio was a main variable to determine the properties, including flowability, extrudability, buildability, and open time. According to the flow test results, the optimized flow of the EVA-modified cementitious mixtures was found to be 65% for buildability. This excellent flowability could be achieved because the flow increased as the EVA/cement ratio increased; conversely, the extrudability was slightly reduced when the EVA/cement ratio increased. However, if the flow of the EVA-modified cementitious mixtures was maintained at 65%, ACE could be achieved without significant issues. In addition, the height of the additive concrete walls created was not substantially reduced after printing of these mixtures, even though different EVA/cement ratios were applied. Plus, ACE can be operated longer with such mixtures because the open time becomes longer as the EVA/cement ratio increases. In summary, the results clearly demonstrated that EVA-modified cementitious mixtures were feasible for use as ACE materials.