This study analyzed the relationship between the degree of conversion (DC), solubility, and salivary sorption of a hybrid (Filtek P 60) and a nanofilled resin composite (Filtek Supreme), and evaluated the influence of the light-activation mode on these properties. Two light-activation modes were used: Conventional (C; 850 mW/cm2 for 20 s) and Soft-start (SS; 100-1,000 mW/cm2 for 10 s + 1,000 mW/cm2 for 10 s). The DC (%) was evaluated by FT-Raman spectroscopy. The solubility and salivary sorption were measured after immersion in artificial saliva for 7 days. Data were analyzed by ANOVA and Student-Newman-Keuls' test and linear regression analysis (α = 0.05). The DC varied from 50.52% (nanofilled composite) to 57.15% (hybrid composite), and was influenced by the light-activation mode: C > SS. The solubility (0.45 μg/mm3) and salivary sorption (8.04 μg/mm3) of the nanofilled composite were greater than those of the hybrid composite (0.40 μg/mm3/ 6.87 μg/mm3), and were influenced by the light-activation mode: SS > C. Correlation was found between DC and solubility (r = - 0.89, p<0.05), as well as between solubility and salivary sorption (r = 0.95). These findings suggest that nanofilled composites may present higher degradation in the oral environment than hybrid ones. Soft-start light-activation mode may increase the solubility of resin composites.

This study evaluated the effects of acidic medicines (Dimetapp® and Claritin®), under pH-cycling conditions, on the surface degradation of four composite resins (microhybrid: TPH, Concept, Opallis and Nanofilled: Supreme). Thirty disc-shaped specimens (Ø = 5.0 mm / thickness = 2.0 mm) of each composite were randomly assigned to 3 groups (n = 10): a control and two experimental groups, according to the acidic medicines evaluated. The specimens were finished and polished with aluminum oxide discs, and the surface roughness was measured by using a profilometer. After the specimens were submitted to a pH-cycling regimen and immersion in acidic medicines for 12 days, the surface roughness was measured again. Two specimens for each material and group were analyzed by scanning electron microscopy (SEM) before and after pH-cycling. Data were analyzed by the Student's-t test, ANOVA, Duncan's multiple range test and paired t-test (α=0.05). Significant increase in roughness was found only for TPH in the control group and TPH and Supreme immersed in Claritin® (p<0.05). SEM analyses showed that the 4 composite resins underwent erosion and surface degradation after being subjected to the experimental conditions. In conclusion, although the roughness was slightly affected, the pH-cycling and acidic medicines caused surface degradation of the composite resins evaluated. Titratable acidity seemed to play a more crucial role on surface degradation of composite resins than pH.

SUMMARY: This in vitro study evaluated the effect of mouth rinses on salivary sorption (Sp), solubility (Sl) and surface degradation of a nanofilled (Z350) and hybrid (P60) resin composite. Specimens (6 mm in diameter and 1 mm thick) of a nanofilled and hybrid resin composite were immersed in artificial saliva at 37°C for seven days. Twice a day, the samples (n=5) were immersed in 20 ml of three mouth rinses: Listerine, Plax Mint and Plax. A control group was maintained in artificial saliva. Sp and Sl were evaluated based on ISO 4049:2000(E) and surface degradation by scanning electron microscopy–SEM. The degree of conversion (DC%) of resin composites was obtained by using an FT-IR spectrometer equipped with an attenuated total reflectance crystal (ATR). The data were analyzed using the Student's t-test, ANOVA and Tukey test for multiple comparisons. No significant difference in DC% was found between the two resin composites (p<0.05). The highest sorption rate was presented by the nanofilled composite exposed to Listerine (p<0.05). The hybrid composite in the control group (artificial saliva) and Plax presented the lowest sorption (p<0.05). The highest solubility was presented by the two resin composites exposed to Listerine (p<0.05). SEM analysis showed that mouth rinses produced more severe surface degradation in the nanofilled composite.

Clinical Relevance: The nanofilled composite presented a lower degree of conversion, flexural modulus and flexural strength than the hybrid composite. On the other hand, the two materials had a similar hardness. The light polymerization mode influenced only the degree of conversion and the hardness of composites.