Conducting polymers and carbon-based materials such as graphene oxide (GO) and activated carbon (AC) are the most promising capacitive materials, though both offer charge storage through different mechanisms. However, their combination can lead to some unusual results, offering improvement in certain properties in comparison with the individual materials. Cycling stability of supercapacitors devices is often a matter of concern, and extensive research is underway to improve this phenomena of supercapacitive devices. Herein, a high-performance asymmetric supercapacitor device was fabricated using graphene oxide–polyaniline (GO@PANI) nanocomposite as positive electrode and activated carbon (AC) as negative electrode. The device showed 142 F g⁻¹ specific capacitance at 1 A g⁻¹ current density with capacitance retention of 73.94% at higher current density (10 A g⁻¹). Most importantly, the device exhibited very high electrochemical cycling stability. It retained 118.6% specific capacitance of the starting value after 10,000 cycles at 3 Ag⁻¹ and with coulombic efficiency of 98.06 %, indicating great potential for practical applications. Very small solution resistance (Rs, 0.640 Ω) and charge transfer resistance (Rct, 0.200 Ω) were observed hinting efficient charge transfer and fast ion diffusion. Due to asymmetric combination, potential window was extended to 1.2 V in aqueous electrolyte, as a result higher energy density (28.5 Wh kg⁻¹) and power density of 2503 W kg⁻¹ were achieved at the current density 1 Ag⁻¹. It also showed an aerial capacitance of 57 mF cm⁻² at current 3.2 mA cm⁻². At this current density, its energy density was maximum (0.92 mWh cm⁻²) with power density (10.47 W cm⁻²).

The synthesis of promising nanocomposite materials can always be tricky and depends a lot on the method of synthesis itself. Developing such synthesis routes, which are not only simple but also can effectively catch up the synergy of the compositing material, is definitely a worthy contribution towards nanomaterial science. Carbon-based materials, such as graphene oxide, and conjugative polymers, such as conductive polyaniline, are considered materials of the 21st century. This study involves a simple one pot synthesis route for obtaining a nanocomposite of polyaniline and graphene oxide with synergistic effects. The study was carried out in a systematic way by gradually changing the composition of the ingredients in the reaction bath until the formation of nanocomposite took place at some particular reaction parameters. These nanocomposites were then utilized for the fabrication of electrodes for aqueous symmetric supercapacitor devices utilizing gold or copper as current collectors. The device manifested a good capacitance value of 264 F/g at 1 A/g, magnificent rate performance, and capacitance retention of 84.09% at a high current density (10 A/g) when gold sheet electrodes were used as the current collectors. It also showed a capacitance retention of 79.83% and columbic efficiency of 99.83% after 2000 cycles.

Methyl red (MR) dye, one of the azo dyes, is mutagenic and its persistence has negative effects on the environment and people’s health. The current work is the first to demonstrate that methyl red dye can be removed effectively and sustainably, utilizing biomass derived from the bark of the Dodonaea viscosa (Hopbush) plant. The Hopbush bark shows effective adsorption of MR, upto 73%, under optimized conditions in an aqueous medium. The experimental conditions were optimized by examining the effect of time, initial dye concentration, pH and ionic strength on the adsorption process in an aqueous medium. Maximum (i.e., 73%) adsorption of MR removal (500 ppm) was observed in highly acidic conditions (pH = 1) at a contact time of 75 min. The pseudo-second-order kinetic model and Freundlich adsorption isotherm appeared to be the most appropriate for characterizing the MR’s adsorption onto the bark of the D. viscosa plant. Furthermore, it was shown that bark powder outperformed animal charcoal, silica gel, and powdered flowers, as well as the leaves of the same species, in terms of adsorption capacity. Thus, a natural adsorbent that is inexpensive and readily available—the bark of the D. viscosa plant—can be used to effectively remove harmful dyes from contaminated water and protect water resources from harmful pollutants.

The presence of dyes in water stream is a major environmental problem that affects aquatic and human life negatively. Therefore, it is essential to remove dye from wastewater before its discharge into the water bodies. In this study, Banyan (Ficus benghalensis, F. benghalensis) tree leaves, a low-cost biosorbent, were used to remove brilliant green (BG), a cationic dye, from an aqueous solution. Batch model experiments were carried out by varying operational parameters, such as initial concentration of dye solution, contact time, adsorbent dose, and pH of the solution, to obtain optimum conditions for removing BG dye. Under optimum conditions, maximum percent removal of 97.3% and adsorption capacity (Qe) value of 19.5 mg/g were achieved (at pH 8, adsorbent dose 0.05 g, dye concentration 50 ppm, and 60 min contact time). The Langmuir and Freundlich adsorption isotherms were applied to the experimental data. The linear fit value, R² of Freundlich adsorption isotherm, was 0.93, indicating its best fit to our experimental data. A kinetic study was also carried out by implementing the pseudo-first-order and pseudo-second-order kinetic models. The adsorption of BG on the selected biosorbent follows pseudo-second-order kinetics (R² = 0.99), indicating that transfer of internal and external mass co-occurs. This study surfaces the excellent adsorption capacity of Banyan tree leaves to remove cationic BG dye from aqueous solutions, including tap water, river water, and filtered river water. Therefore, the selected biosorbent is a cost-effective and easily accessible approach for removing toxic dyes from industrial effluents and wastewater.