Acid-soluble collagen (ASC) and pepsin-soluble collagen (PSC) from the skin of river puffer (ASC-RP and PSC-RP) and tiger puffer (ASC-TP and PSC-TP) were extracted and physicochemically examined. Denaturation temperature (T_d) for all the collagens was found to be 25.5–29.5 °C, which was lower than that of calf skin collagen (35.9 °C). Electrophoretic patterns indicated all four samples were type I collagen with molecular form of (α₁)₂α₂. FTIR spectra confirmed the extracted collagens had a triple-helical structure, and that the degree of hydrogen bonding in ASC was higher than PSC. All the extracted collagens could aggregate into fibrils with D-periodicity. The fibril formation rate of ASC-RP and PSC-RP was slightly higher than ASC-TP and PSC-TP. Turbidity analysis revealed an increase in fibril formation rate when adding a low concentration of NaCl (less than 300 mM). The fibril formation ability was suppressed with further increasing of NaCl concentration, as illustrated by a reduction in the turbidity and formation degree. SEM analysis confirmed the well-formed interwoven structure of collagen fibrils after 24 h of incubation. Summarizing the experimental results suggested that the extracted collagens from the skin of river puffer and tiger puffer could be considered a viable substitute to mammalian-derived collagens for further use in biomaterial applications.

Acid-solubilized (ASC) and pepsin-solubilized collagen (PSC) extracted at 4 °C (ASC-4 and PSC-4), 12 °C (ASC-12 and PSC-12), and 20 °C (ASC-20 and PSC-20) from the skin of farmed pufferfish (Takifugu obscurus) was characterized by SDS-polyacrylamide gel electrophoresis (SDS-PAGE), Fourier-transform infrared spectroscopy (FTIR), and fibril-forming tests. The results indicate that extraction at 12 °C can effectively improve the extraction efficiency of natural collagen compared with extraction at 4 °C. However, extraction at 20 °C results in a decrease in molecular integrity, thus, inducing the resultant collagen to degrade or even lose fibril-forming ability. Transmission electron microscope (TEM) images revealed that ASC-4, PSC-4, ASC-12, and PSC-12 can assemble into fibrils with D-periodicities, and ASC-20 associated into molecular aggregates alongside partial D-banded fibrils, while no well-defined fibrils were observed in PSC-20. Scanning electron microscope (SEM) analysis confirmed the well-defined fibril morphologies of ASC-4, PSC-4, ASC-12, and PSC-12 with imino acid contents between 190.0 and 197.8 residues/1000 residues. The denaturation temperature of ASC-4, PSC-4, ASC-12 and PSC-12 was 30.0, 27.6, 25.9 and 22.7 °C, respectively. This study indicates that ASC and PSC extracted at 4 °C and 12 °C could be alternatives to terrestrial collagens for industrial applications.