For the development of thick film graphite electrodes, a 3D battery concept is applied, which significantly improves lithium-ion diffusion kinetics, high-rate capability, and cell lifetime and reduces mechanical tensions. Our current research indicates that 3D architectures of anode materials can prevent cells from capacity fading at high C-rates and improve cell lifespan. For the further research and development of 3D battery concepts, it is important to scientifically understand the influence of laser-generated 3D anode architectures on lithium distribution during charging and discharging at elevated C-rates. Laser-induced breakdown spectroscopy (LIBS) is applied post-mortem for quantitatively studying the lithium concentration profiles within the entire structured and unstructured graphite electrodes. Space-resolved LIBS measurements revealed that less lithium-ion content could be detected in structured electrodes at delithiated state in comparison to unstructured electrodes. This result indicates that 3D architectures established on anode electrodes can accelerate the lithium-ion extraction process and reduce the formation of inactive materials during electrochemical cycling. Furthermore, LIBS measurements showed that at high C-rates, lithium-ion concentration is increased along the contour of laser-generated structures indicating enhanced lithium-ion diffusion kinetics for 3D anode materials. This result is correlated with significantly increased capacity retention. Moreover, the lithium-ion distribution profiles provide meaningful information about optimizing the electrode architecture with respect to film thickness, pitch distance, and battery usage scenario.

In situ scanning electron microscopy (SEM) offers a good way to investigate the structural evolution during lithiation and delithiation processes. In this paper, the dynamical morphological evolution of 3D-line-structured/unstructured Si/C composite electrodes was observed by in situ SEM. The investigation revealed the microstructural origin of large charge capacity for 3D-line-structured anodes. Based on this proposed mechanism, a coarse optimization of 3D-line-structured anodes was proposed. These results shed light on the unique advantages of using an in situ SEM technique when studying realistic bulk batteries and designing 3D electrode structures.

The 3D battery concept applied on silicon–graphite electrodes (Si/C) has revealed a significant improvement of battery performances, including high-rate capability, cycle stability, and cell lifetime. 3D architectures provide free spaces for volume expansion as well as additional lithium diffusion pathways into the electrodes. Therefore, the cell degradation induced by the volume change of silicon as active material can be significantly reduced, and the high-rate capability can be achieved. In order to better understand the impact of 3D electrode architectures on rate capability and degradation process of the thick film silicon–graphite electrodes, we applied laser-induced breakdown spectroscopy (LIBS). A calibration curve was established that enables the quantitative determination of the elemental concentrations in the electrodes. The structured silicon–graphite electrode, which was lithiated by 1C, revealed a homogeneous lithium distribution within the entire electrode. In contrast, a lithium concentration gradient was observed on the unstructured electrode. The lithium concentration was reduced gradually from the top to the button of the electrode, which indicated an inhibited diffusion kinetic at high C-rates. In addition, the LIBS applied on a model electrode with micropillars revealed that the lithium-ions principally diffused along the contour of laser-generated structures into the electrodes at elevated C-rates. The rate capability and electrochemical degradation observed in lithium-ion cells can be correlated to lithium concentration profiles in the electrodes measured by LIBS.