Materials genome engineering databases represent fundamental infrastructures for data-driven materials design, in which the data resources should satisfy the FAIR (Findable, Accessible, Interoperable and Reusable) principles. However, a variety of challenges, such as data standardization, veracity and longevity, still impede the progress of data-driven materials science, including both high-throughput experiments and simulations. In this work, we propose a metadata schema for lattice thermal conductivity from first-principles calculations. The calculation workflow for lattice thermal conductivity includes structural optimization and the calculation of interatomic force constants and lattice thermal conductivity. The data generated during the calculation process corresponds to the virtual sample information, virtual source data and processed data, respectively, as specified in the General rule for materials genome engineering data of the Chinese Society for Testing and Materials. Following this general rule, the metadata structure and schema for each action are systematically defined and all metadata elements can be collected completely. Although this metadata schema is specific to lattice thermal conductivity calculations, it provides general rules and insights for other computational materials data in materials genome engineering.

Ceria-modified Pt/Al₂O₃ catalyst has been commonly prepared by the impregnation of platinum on ceria-modified alumina and widely applied in the chemical industry and automotive industry. The in situ diffuse reflectance infrared Fourier transformed spectroscopy (DRIFTS), and thermogravimetric (TG) analysis techniques were employed to investigate the typical mechanisms of the bis(ethanolammonium)hexahydroxyplatinate(IV) and cerium nitrate decomposition catalyzed by Pt^δ+ species for the facile synthesis of CeO₂-Pt/Al₂O₃ catalyst. It was found that Pt⁴⁺-catalyzed decomposition of cerium nitrate leads to the higher dispersity of ceria and forming more active oxygen species, on the basis of X-ray diffraction (XRD) and H₂ temperature-programmed reduction (H₂-TPR) results. The in situ activity measurements were also performed to investigate the reaction mechanisms and the specific activities for the catalytic CO, NO, C₃H₆ and C₃H₈ co-oxidation. The results indicate that undesirable N₂O by-product is formed by the selective catalytic reduction (SCR) of NO by C₃H₆ below 350 °C. The cerium addition effectively improves the activity of catalytic oxidation, but exhibits an increased N₂O yield, due to the increased reducibility.