An accurate prediction of temperature and stress evolution in work rolls is crucial to assess the service life of the work roll. In this paper, a finite element method (FEM) model with a deformable work roll and a meshed, rigid body considering complex thermal boundary conditions over the roll surface is proposed to assess the temperature and the thermal stress in work rolls during hot rolling and subsequent idling. After that, work rolls affected by the combined action of temperature gradient and rolling pressure are investigated by taking account of the hot strip. The accuracy of the proposed model is verified through comparison with the calculation results obtained from the mathematical model. The results show that thermal stress is dominant in the bite region of work rolls during hot rolling. Afterwards, the heat treatment residual stresses which are related to thermal fatigue are simulated and introduced into the work roll as the initial stress to evaluate the redistribution under the thermal cyclic loads during the hot rolling process. Results show that the residual stress significantly changed near the roll surface.

Considerable residual stress is produced during heat treatment. Compressive residual stress at the shell is conductive to improving the thermal fatigue life of a work roll, while tensile stress in the core could cause thermal breakage. In hot rolling, thermal stress occurs under the heating-cooling cycles over the roll surface due to the contact with the hot strip and water spray cooling. The combination of thermal stress and residual stress remarkably influences the life of a work roll. In this paper, finite element method (FEM) simulation of hot rolling is performed by treating the residual stress as the initial stress. Afterwards, the effects of the initial roll temperature and cooling conditions on thermal stress considering the initial residual stress are discussed. Lastly, the thermal fatigue life of a work roll is estimated based on the strain life model. The higher initial roll temperature causes a higher temperature but a lower compressive thermal stress at the roll surface. The surface temperature and compressive stress increase significantly in the insufficient cooling conditions, as well as the center tensile stress. The calculation of the fatigue life of a work roll based on the universal slopes model according to the 10% rule and 20% rule is reasonable compared with experimental results.

Work rolls used for hot strip rolling undergo the cyclic sequence of heating-cooling over the roll surface due to contact with the hot strip and the following cooling systems during every rolling revolution. Severe temperature gradient and thermal stress caused by cyclic heating-cooling loading are dominant factors for thermal fatigue failure of work rolls. Therefore, investigations on temperature and thermal stress-strain are essential for understanding the thermal fatigue of work roll. In this study, a thermo-mechanical analysis with elastic-plastic material parameters via a simplified finite element model is carried out to compute the stress-strain range experienced by the work roll during rolling and idling. Then, a model with the initial crack in the roll surface considering different depths and a model with the hot strip is conducted to better understand the thermal behaviors of the work roll during hot rolling respectively. Furthermore, the thermal fatigue life of work roll is assessed based on the modified Coffin-Manson relation, considering the effect of multi-axial stress state and temperature-dependent material properties caused by temperature fluctuations in work roll during hot rolling.