The fabrication of high purity copper using additive manufacturing has proven difficult because of oxidation of the powder feedstock. Here, we present work on the hydrogen heat treatment of copper powders for electron beam powder bed fusion (EB-PBF), in order to enable the fabrication of high purity copper components for applications such as accelerator components and vacuum electronic devices. Copper powder with varying initial oxygen contents were hydrogen heat-treated and characterized for their chemistry, morphology, and microstructure. Higher initial oxygen content powders were found to not only reduce surface oxides, but also reduce oxides along the grain boundaries and form trapped H₂O vapor inside the particles. The trapped H₂O vapor was verified by thermogravimetric analysis (TGA) and residual gas analysis (RGA) while melting. The mechanism of the H₂O vapor escaping the particles was determined by in-situ SEM heated stage experiments, where the particles were observed to crack along the grain boundaries. To determine the effect of the EB-PBF processing on the H₂O vapor, the thermal simulation and the validation of single melt track width wafers were conducted along with melting single layer discs for chemistry analysis. A high speed video of the EB-PBF melting was performed in order to determine the effect of the trapped H₂O vapor on the melt pool. Finally, solid samples were fabricated from hydrogen-treated copper powder, where the final oxygen content measured ~50 wt. ppm, with a minimal residue hydrogen content, indicating the complete removal of trapped H₂O vapor from the solid parts.

Permanent magnets without rare earth (RE) elements, such as alnico, will improve supply stability and potentially decrease permanent magnet cost, especially for traction drive motors and other increased temperature applications. Commercial alnico magnets with the highest energy product are produced by directional solidification (DS) to achieve a columnar grain orientation followed by significant final machining, adding to the high cost. Additive manufacturing (AM) is an effective method to process near net-shape parts with minimal final machining of complex geometries. AM also, has potential for texture/grain orientation control and compositionally graded structures. This report describes fabrication of alnico magnets by AM using both laser engineered net shaping (LENS)/directed energy deposition (DED) and electron beam melting powder bed fusion (EBM/PBF). High pressure gas atomized (HPGA) pre-alloyed alnico powders, with high purity and sphericity, were built into cylindrical and rectangular samples, followed by magnetic annealing (MA) and a full heat treatment (FHT). The magnetic properties of these AM processed specimens were different from their cast and sintered counterparts of the same composition and show a great sensitivity to heat treatment. The AM process parameters used in this developmental study did not yet result in any preferred texture within the alnico AM builds. These findings demonstrate feasibility for near net-shape processing of alnico permanent magnets for use in next generation traction drive motors and other applications requiring increased operating temperatures and/or complex engineered part geometries, especially with further AM process development for texture control.