In this work, experimental and numerical analyses of repairs on carbon fiber reinforced epoxy (CFRE) substrates, with CFRE and aluminum alloy doublers typical of aircraft structures, are presented. The substrates have a bridge gap of 12.7 mm (simulated crack), repaired with twin doublers joined with riveted, adhesive bonded, and hybrid joints. The performance of the repairs using different doubler materials and joining techniques are compared under static loading. The experimental results show that riveted joints have the lowest strength, while adhesive bonded joints have the highest strength, irrespective of the doubler material. Finite element analysis (FEA) of the studied joints is also performed using commercial FEA tool Abaqus. In the FEA model, point-based fasteners are used for the rivets, and a cohesive zone contact model is used to simulate the adhesive bond. The FEA results indicate that the riveted joints have higher tensile stresses on the metal doublers compared to the composite doublers. As per the failure modes, interestingly, for hybrid joints using composite doublers, the doublers fail due to net-section failure, while, for hybrid joints using metal doublers, it is the composite substrate that fails due to net-section failure. This suggests vulnerability of the composite structures to mechanical fastener holes. Lastly, the Autodesk Helius composite tool is used for prediction of first-ply failure and ply load distribution, and for progressive failure analysis of the composite substrate.

Aircraft lap joints play an important role in minimizing the operational cost of airlines. Hence, airlines pay more attention to these technologies to improve efficiency. Namely, a major time consuming and costly process is maintenance of aircraft between the flights, for instance, to detect early formation of cracks, monitoring crack growth, and fixing the corresponding parts with joints, if necessary. This work is focused on the study of repairs of cracked aluminium alloy (AA) 2024-T3 plates to regain their original strength; particularly, cracked AA 2024-T3 substrate plates repaired with doublers of AA 2024-T3 with two configurations (riveted and with adhesive bonding) are analysed. The fatigue life of the substrate plates with cracks of 1, 2, 5, 10 and 12.7mm is computed using Fracture Analysis 3D (FRANC3D) tool. The stress intensity factors for the repaired AA 2024-T3 plates are computed for different crack lengths and compared using commercial FEA tool ABAQUS. The results for the bonded repairs showed significantly lower stress intensity factors compared with the riveted repairs. This improves the overall fatigue life of the bonded joint.